1) thermolytic
热分解氧化法
1.
The composite material silica-ruthenium dioxide was prepared through thermolytic oxidation for the film electrodes of supercapacitor, taking RuCl_3·xH_2O mixed with TEOS as raw material and Ti slide as substrate.
以水合三氯化钌和正硅酸乙酯为原料,以钛片为基底,采用热分解氧化法制备了二氧化硅/氧化钌复合膜电极,利用扫描电子显微镜观察电极表面形貌,利用循环伏安曲线法研究电极的电容性能·考察了原料配比,烧结温度,烧结时间等制备条件对电极电容性能的影响·结果发现,二氧化硅/氧化钌复合膜电极具有优良的电容性能,当水合三氯化钌与正硅酸乙酯的物质的量的比为5∶2,烧结温度为350℃,烧结时间为1h时单电极的比容量最高可达137mF·cm-2,比文献值提高了近3个数量级
2) oxidation-thermal decomposition reaction
氧化热分解
3) The thermal decompositiom process of complex peroxide
过氧化物热分解法
4) thermal decomposition-oxidation-deoxidization
热分解氧化还原
1.
In this article, Fe, Fe-Co and Fe-Ni magnetic fibers are prepared by thermal decomposition-oxidation-deoxidization method of gel precursor fibers.
本文以柠檬酸铁、金属盐和氨水为原料,采用凝胶前驱体纤维热分解氧化还原法制备了铁、铁-钴、铁-镍三种磁性纤维。
5) thermal oxidizing decomposition
氧化热解
1.
Thermogravity analysis technique was used to study the course of thermal oxidizing decomposition from normal temperature to ignition temperature for the coal.
运用热重分析手段对煤从常温到燃点之间的氧化热解过程进行了研究,运用不同动力学机制模型函数分别对热重分析数据进行了处理和相关性分析。
6) oxidative pyrolysis
部分氧化裂解法
补充资料：热氧化降解塑炼法
分子式：
分子量：
CAS号：
性质：利用加热氧化法提高橡胶可塑性的一种塑炼过程。一般使用于普通丁苯橡胶。先将橡胶切成细条，放于塑炼罐内，在约150℃和压缩空气压力0.196~0.294兆帕（2~3公斤力/厘米2）下进行。时间根据不同可塑性要求而定。为了使质量均匀，还往往用机械进行补充加工。如果单是加热或在惰性气体介质中进行热塑炼，则所得素炼胶的可塑性低而不稳定。
分子量：
CAS号：
性质：利用加热氧化法提高橡胶可塑性的一种塑炼过程。一般使用于普通丁苯橡胶。先将橡胶切成细条，放于塑炼罐内，在约150℃和压缩空气压力0.196~0.294兆帕（2~3公斤力/厘米2）下进行。时间根据不同可塑性要求而定。为了使质量均匀，还往往用机械进行补充加工。如果单是加热或在惰性气体介质中进行热塑炼，则所得素炼胶的可塑性低而不稳定。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。