The low cycle fatigue (LCF) and steady cycle stress vs strain behavior of directionally solidified DZ4 superalloy at 760℃ and 800℃ are studied.
对定向凝固DZ4合金760℃和800℃下的低周疲劳和稳定循环应力应变行为进行了研究,并结合断口观察试验结果,对其疲劳裂纹的萌生与扩展进行了分析。
2) steady state circulation flow
稳定循环
1.
The characteristics of steady state circulation flow in a single loop oscillating heat pipe have been analyzed from a thermo-mechanical viewpoint.
以简单回路振荡热管为热力系统,通过热力学分析,导出了稳定循环的条件:蒸发端吸热量等于冷凝端放热量,且必须考虑耗散功的影响作用。
2.
The heat balance and characteristics of steady state circulation flow of a single loop pulsating heat pipe was studied with thermo-mechanical analysis.
以简单回路脉动热管为热力系统,通过热力学分析,导出了系统的热平衡条件和稳定循环的特征,得到系统耗散功和系统体积功的关系,以及用水作为工质时膨胀功与汽化压力的关系。
3.
The theoretical model was established to describe steady state circulation flow of a single loop pulsating heat pipe(PHP)with thermo-mechanical and hydrodynamics analysis.
分析显示,稳定循环时,系统循环体积功用于克服系统循环耗散功,而系统循环耗散功(热)与热管传热量呈一定关系。
3) cyclic stability
循环稳定性
1.
1) on electrochemical cyclic stability of La2Mg1-xAlxNi7.
5贮氢合金电化学循环稳定性的影响。
2.
In order to improve the cyclic stability of La-Mg-Ni system,as-cast La0.
为了改善La-Mg-Ni系合金电极的循环稳定性,对铸态合金La0。
3.
3Al0 2 was prepared by twin-roll process, and the microstructure, capacity and cyclic stability of the alloy were characterized by SEM, XRD and constant current charge and discharge.
使用双辊淬冷技术制备了LaNi5基AB5型贮氢合金,用扫描电镜和X射线衍射确定合金的晶粒尺寸,用恒电流充放电方法确定合金的电化学容量及其循环稳定性。
4) cycling stability
循环稳定性
1.
The results show that with Co being substituted by suitable amounts of Cu,Cr,Zn and Fe,the low Co hydrogen storing alloys can have high discharge capacity and good cycling stability.
为了降低贮氢合金中的钴含量,从而降低镍氢电池的价格,在贮氢合金M1Ni3 55Co0 75Al0 3Mn0 4的基础上,依次添加Cu、Cr、Zn、Fe元素,得到稀土基多元贮氢合金,并对其放电容量和循环稳定性进行了测试和分析。
2.
The results show that a partial substitution of Co by a small amount of iron, copper and chromium is very effective in improving the electrochemical cycling stability in the La(NiMnCoAl) 5 Alloy.
结果显示 ,用少量的铁、铜和铬部分取代贮氢合金La(NiMnCoAl) 5中的钴对改善贮氢合金电化学循环稳定性有效。
3.
In this paper, several reasons for fading have been analyzed, and its degraded cycling stability and some methods to hinder its capacity fading have also been discussed in order to improve the charge-discharge characteristic.
本文对引起LiMn2O4循环稳定性衰减的原因进行了分析,并综述了当前抑制循环容量衰减、提高电性能的方法。
5) cycle stability
循环稳定性
1.
Influence of melt spinning on the cycle stability of La_(0.75-x)Zr_xMg_(0.25)Ni_(3.2)Co_(0.2)Al_(0.1)(x=0～0.2) electrode alloys
熔体快淬对La_(0.75-x)Zr_xMg_(0.25)Ni_(3.2)Co_(0.2)Al_(0.1)(x=0～0.2)电极合金循环稳定性的影响
2.
And their discharge capacity,cycle stability and their microstructure are determined and analyzed.
3的基础上,依次添加铜、铬、锌及铁元素,得到稀土基多元贮氢合金,并测试和分析了它们的放电容量、循环稳定性以及微观结构。
3.
The microstructures of the as-cast and quenched alloys were analyzed by XRD, SEM and TEM, and electrochemical cycle stability of the as-cast and quenched alloys were measured.
6)贮氢合金,用XRD,TEM及SEM观测了铸态及快淬态的微观结构,测试了合金在铸态及快淬态下的电化学循环稳定性。
6) stable domains cycle
稳定域循环
补充资料：轧辊残余应力(见轧辊应力)
轧辊残余应力(见轧辊应力)
residual stresses in roll
zhagun eanyu yingli轧辊残余应力(residual stresses in roll)见礼辐应力。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条