1) Antiferromagnetic Austenite
反铁磁性奥氏体
2) austenitic cast iron
奥氏体铸铁
1.
A austenitic cast iron is produced by selecting the components of low-aluminum low-nickel middle-manganese and using the technology of silicon iron-aluminum recombination instantaneous inoculation.
通过选择低铝低镍中锰成分和采用硅铁 铝复合瞬时孕育工艺生产了奥氏体铸铁 ,其组织由A型石墨、奥氏体基体及数量小于 15 %、均匀分布的粒状碳化物组成。
2.
Corrosion behaviours of austenitic cast iron and 18 8 stainless steel in hot concentrated caustic soda solution were investigated by means of weight loss and electrochemical measurement.
用失重法和电化学方法研究了奥氏体铸铁和１８ － ８ 不锈钢在高温烧碱中的腐蚀行为。
3) austenitic nodular castiron
奥氏体球铁
4) austenite cast iron
奥氏体生铁
5) austenoferritic steel
奥氏体铁素体钢
6) austenitic-ferrite
奥氏体-铁素体
1.
Therefore, the study austenitic - ferrite phase change the dynamics and thermodynamics, the establishment of materials processing technology with the organization of the state of quantitative relations, design and material composition of processing technology to control access to the material requested by the performance is very important Significance.
奥氏体-铁素体相变是钢铁材料制备、加工和热处理过程中发生的一种很普遍的物理冶金现象。
补充资料：反铁磁性
在原子自旋（磁矩）受交换作用而呈现有序排列的序磁材料中,如果相邻原子自旋间因受负的交换作用,自旋为反平行排列，则磁矩虽处于有序状态(称为序磁性)，但总的净磁矩在不受外场作用时仍为零。这种磁有序状态称为反铁磁性。温度升高，热扰动会破坏磁矩的有序排列。热扰动完全破坏反铁磁有序的温度称为奈耳温度或奈耳点θN。在宏观磁性上，反铁磁体为弱磁体，磁化率在奈耳点出现极大值。反铁磁体也具有磁畴结构，已由实验观测到。在微观结构上，反铁磁体中磁矩反平行排列的磁结构也已由中子衍射所证实。如MnO(θN=122K)、FeF2(θN=79K)、α-Mn(θN≈100K)、Cr(θN=331K)都是已由中子衍射测定其磁结构的反铁磁体。一些反铁磁体在强外场或低温下转变为磁矩平行排列的铁磁体，这种序磁性称为变磁性。还有些反铁磁体如稀土金属中的铽、镝、钬的磁矩呈圆锥形螺旋排列，磁矩有序而净磁矩为零，称为螺旋型反铁磁性（螺旋磁性的一种）或非共线型反铁磁性。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。