1) pulverized slag of high titanium content
磨细高钛矿渣
1.
Tests and researches were made to use the pulverized slag of high titanium content as an ingredient in concrete and the results show that the addition of the pulverized titanium slag has improved remarkably the workability of the concrete and enhanced greatly the compressive strength of the concrete.
文章中论述了将磨细高钛矿渣作为混凝土的一种配制原料,进行了相关的试验研究。
3) high-titanium slag
高钛矿渣
1.
Study on grindability of harding high-titanium slag;
水淬高钛矿渣的粉磨性能研究
2.
Impact of high-titanium slag on performance of cement-based composites
高钛矿渣对水泥基复合材料性能的影响
4) GGBS
磨细矿渣
1.
Concrete crack mending material was prepared by Micro-fine Cement(MC),Granulated Ground Blast Furnace Slag(GGBS) and other admixtures.
以超细水泥、磨细矿渣及其它外加剂制备了水泥混凝土路面裂缝灌浆材料,研究了该类材料的耐久性能和收缩性能,并通过热分析及微观形貌的观测分析揭示了材料耐久性的改性机理。
2.
From the point of view of engineering application and taking the GGBS and the composite mineral admixture which contains GGBS and FA as research objective,influence of the mineral admixtures on the performances such as durability and mechanical properties of the cementitious material is investigated.
本课题从工程应用的角度出发,以磨细矿渣和磨细矿渣-粉煤灰复合掺合料为研究对象,着重研究了矿物掺合料对水泥基材料耐海水侵蚀性能的影响。
3.
The chloride binding capability of mortar and paste blended with 70% ground granulated blast furnace slag (GGBS) is greatly increased, especially the chemical binding capability.
研究了磨细矿渣净浆和砂浆对外渗氯离子的结合性能 ,结果表明 :掺加 70 %磨细矿渣可使净浆和砂浆结合氯离子能力、尤其是化学结合能力大幅度增加 。
5) ground slag
磨细矿渣
1.
Application of the fly ash and ground slag on marine concrete
粉煤灰和磨细矿渣在海工混凝土中的应用
2.
Effect of ground slag to hydration properties of different cement fineness
磨细矿渣对不同细度水泥水化性能的影响
3.
The influences of the fly ash and ground slag on performances of the strength,contraction,frost-resistance,impervious of Cl-and elasticity modulus of the LC45 light-weight concrete was researched.
研究了LC45高强轻集料混凝土掺加磨细矿渣和粉煤灰后,在强度、收缩、抗冻、抗氯离子渗透性能以及弹性模量方面的影响。
6) ground granulated blast furnace slag
磨细矿渣
1.
It is found that fly Ash(FA)reduce Autogenous shrinkage,silica fume(SF)and ground granulated blast furnace slag(GBS)increases Autogenous shrinkage.
为了探讨复合矿物质超细粉对水泥石自收缩的影响规律,将硅灰与粉煤灰、磨细矿渣与粉煤灰2种复合掺合料分别加入水泥浆体中,通过改变粉煤灰与硅灰的质量比、粉煤灰与磨细矿渣的质量比。
2.
The performance of ground granulated blast furnace slag to resist the chloride corrosion is analyzed by the internal chloride e.
为此 ,分析了去冰盐破坏水泥混凝土路面的机理 ,采用实验室内掺氯离子压滤试验法评价和模拟水泥混凝土路面抗去冰盐腐蚀性能 ,并通过压滤法分析了磨细矿渣抗氯离子侵蚀性
3.
After 90 day s curing in 20℃ water, through accelerated freeze-thaw test, the frost resistance of HSC and SFRHSC specimens, with 20% weight of fly ash, silica fume or ground granulated blast furnace slag (GGBFS), were strdied.
采用快冻试验方法 ,研究了掺量分别为20%粉煤灰、硅灰以及磨细矿渣的高强混凝土(HSC)与钢纤维高强混凝土(SFRHSC) ,在标准养护室内浸水养护90天的抗冻性 ,以及在氯盐侵蚀与冻融循环双重因素作用下的抗冻耐久性。