1) high density polyethylene
高聚乙烯
2) Polymer
高聚物
1.
Transition from a Rubbery Elastic State to a Fluid State of Polymer;
高聚物从高弹态到流体态的转变
2.
Research Progress in Banded Spherulites of Polymers;
高聚物环带球晶的研究进展
3.
Experiments on a new kind polymer-inhibitor for suppressing coal spontaneous ignition;
新型高聚物煤自燃阻化剂的试验研究
3) high degree of polymerization
高聚合度
1.
The optimum polymerization technique for the preparation PVAc with high degree of polymerization was determined by a lot of experiments.
采用醋酸乙烯酯为单体,以OP-10和十二烷基硫酸钠为复配乳化剂,偶氮二脒基丙烷盐酸盐为引发剂,通过正交实验研究了乳液聚合法制备高聚合度聚醋酸乙烯酯的最佳工艺条件。
4) high polymerization degree
高聚合度
1.
Studies on shortening polymerization period of PVC paste resins with high polymerization degree;
缩短高聚合度PVC糊树脂聚合时间的研究
5) polymers
高聚物
1.
Preparation and Application of Polymers Ultrafine Powders;
高聚物超细微粉的制备及应用
2.
An Accelerated Characterization of the Long-term Creep Behavior of Polymers;
高聚物长期蠕变性能的加速表征
6) non-polymer
非高聚物
参考词条
补充资料：高强聚乙烯纤维
分子式：
分子量：
CAS号：
性质：一种由超高分子量（M-W>106）聚乙烯纺制的超高强度的合成纤维。密度0.97，抗拉强度2.0-3.5吉帕，杨氏模量50-125吉帕，断裂伸长率3%-6%。是一种可与碳纤维、芳纶等高强度纤维媲美的合成纤维新品种。其优点是具有极佳的化学稳定性和很高的抗紫外辐射性及生物相容性，但缺点是熔点低（仅140℃），明显低于其他高强纤维。其主要用途是制作海洋工业用的网绳、缆绳，军用防弹材料、耐压容器、人造关节、韧带，体育用品及光导纤维的结构材料等。可用萘、石蜡油等溶剂溶解高分子量的聚乙烯，然后采用凝胶纺丝法纺制。
分子量：
CAS号：
性质：一种由超高分子量（M-W>106）聚乙烯纺制的超高强度的合成纤维。密度0.97，抗拉强度2.0-3.5吉帕，杨氏模量50-125吉帕，断裂伸长率3%-6%。是一种可与碳纤维、芳纶等高强度纤维媲美的合成纤维新品种。其优点是具有极佳的化学稳定性和很高的抗紫外辐射性及生物相容性，但缺点是熔点低（仅140℃），明显低于其他高强纤维。其主要用途是制作海洋工业用的网绳、缆绳，军用防弹材料、耐压容器、人造关节、韧带，体育用品及光导纤维的结构材料等。可用萘、石蜡油等溶剂溶解高分子量的聚乙烯，然后采用凝胶纺丝法纺制。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。