1) mullite nanocrystal
莫来石纳米晶
1.
the change of binder in heat treating is:amorphous solid → microcontent γ-Al2O3(970 ℃) → Al-Si spinel(1030 ℃) → mullite and Al-Si spinel(1150 ℃) → mullite nanocrystal(1250℃).
75mV;粘结剂在烧结过程中经历了如下变化:无定形物质→微量γ-Al2O3(970℃)→铝硅尖晶石(1030℃)→莫来石与铝硅尖晶石(1150℃)→莫来石纳米晶(1250℃)。
2) multi-phase mullite nanocrystal
复相莫来石纳米晶体
3) mullite nanocomposite
莫来石复相纳米晶体
1.
The mullite oxides were further synthesized into mullite nanocomposite using the open-system hydrothermal crystallization method.
0mol/L,在0～80℃升温1h,达到80℃后恒温2h,制备出粒径尺寸在80～100nm,颗粒均匀、分散性好、耐高温的莫来石复相纳米晶体。
4) nano-mullite
纳米莫来石
1.
Polystyrene/nano-mulite composites had been developed based on PS blended with nano-mullite particles.
采用优质煤系高岭土煅烧制备的纳米莫来石(nano-mullite)对聚苯乙烯(polystyrene)进行改性,通过机械共混的方法制备了PS/nano-mullite复合材料。
2.
In this paper,we systematically introduced the current situation and prospect of exploiting mineral nano-material such as nano-kaolinite,nano-calcination-kaolinite,nano-mullite composite oxide,nano-mullite etc series product produced by natural kaolinite in China.
本文较系统地介绍了我国利用天然高岭土生产制备纳米高岭土、纳米煅烧高岭土、纳米莫来石复合氧化物、纳米高纯莫来石等矿物纳米材料系列产品的开发应用现状及其前景展望,指出利用高岭土制备矿物纳米材料是我国高岭土深加工工业的重点发展方向。
3.
The properties of PS filled with nano-mullite,made from high quality Kaoline,were studied.
采用优质煤系高岭土煅烧制备的纳米莫来石(nano-mullite)对聚苯乙烯(PS)进行改性研究,通过机械共混的方法制备了nano-mullite/PS复合材料。
5) nanomullite
纳米莫来石
1.
Nanomullite/PP composites containing 1 wt%,3 wt%,5 wt%,7 wt% and 10 wt% nanomullite were prepared by melt compounding in a two screw extruder.
在双螺杆挤出机中用熔融共混工艺制备纳米莫来石/聚丙烯(PP)复合材料,莫来石的含量为1%、3%、5%、7%和10%。
2.
Nanomullite/PP composites containing 1 wt%,3 wt%,5 wt%,7 and 10 wt% nanomullite were prepared by melt compounding in a two screw extruder.
在双螺杆挤出机中采用熔融共混工艺制备了纳米莫来石填充聚丙烯(PP)复合材料,莫来石的质量含量为1%、3%、5%、7%和10%。
6) mullite naopowder
莫来石纳米粉体
1.
In this paper, the mullite naopowders were preparde by sol gel and supercritical fluid drying (SCFD) methods.
本文采用溶胶 (Sol) 凝胶 (Gel) 超临界流体干燥 (SCFD)法合成了莫来石纳米粉体 ,并利用Tween80表面活性剂调控正硅酸乙酯 (TEOS)的水解缩聚反应过程 ,对溶胶胶粒表面进行修饰 ,以获得在一定范围内可控结构和可控粒度的莫来石纳米微粒。
补充资料：多晶莫来石晶须(纤维)
分子式：
CAS号：
性质：莫来石相为主晶相的多晶纤维。化学成分为Al2O3 72％～77％，SiO222％～17％，B2O3 3％～5％，P2O51.5％～3.0％。纤维直径2～7μm，纤维长度20～125μm。使用温度1350℃。多采用溶胶-凝胶法制造。主要用作补强填料，也可作为轻质、隔热保温材料使用。
CAS号：
性质：莫来石相为主晶相的多晶纤维。化学成分为Al2O3 72％～77％，SiO222％～17％，B2O3 3％～5％，P2O51.5％～3.0％。纤维直径2～7μm，纤维长度20～125μm。使用温度1350℃。多采用溶胶-凝胶法制造。主要用作补强填料，也可作为轻质、隔热保温材料使用。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。