1) Multi-Arc Ion Plating
多弧离子镀膜机
1.
Application of PLC on the Multi-Arc Ion Plating System;
PLC在多弧离子镀膜机系统中的应用研究
2) Multi arc ion coating equipment
多弧离子镀膜设备
3) arc ion plating
多弧离子镀
1.
Ti70Al30N and graded(Ti,Al)N coatings were deposited on 1Cr11Ni2W2MoV martensitic stainless steel by arc ion plating.
采用多弧离子镀技术在马氏体不锈钢1Cr11Ni2W2MoV表面分别沉积Ti70Al30N及梯度(Ti,Al)N涂层。
2.
A NiCoCrAlY coating was deposited on a Ni-base superalloy K417G by arc ion plating.
用多弧离子镀在镍基高温合金K417G上制备了NiCoCrAlY涂层,对涂层进行了1050℃真空退火4小时、粉末包覆渗铝、1100℃下预氧化1小时等后续预处理;研究了涂层在1000℃下的高温氧化行为。
3.
The cavitation erosion behavior of TiN, CrN and (Ti,Cr)N hard coatings produced by arc ion plating on the surface of grey cast iron was studied with an ultrasonic cavitation erosion testing apparatus and a scanning electron microscope.
利用磁致伸缩振动空蚀试验装置 ,研究了灰口铸铁表面多弧离子镀 Ti N、Cr N及 (Ti,Cr) N硬质膜的抗空蚀性能 。
4) multi-arc ion plating
多弧离子镀
1.
Wear resistance of hard coatings plated on 45 steel substrate by multi-arc ion plating;
45~#钢多弧离子镀硬质涂层的耐磨性
2.
Preparation and ultra micro-hardness of TiN/AlN nano-multilayer deposited by multi-arc ion plating;
多弧离子镀制备TiN/AlN纳米多层膜及其超硬效应
3.
Research on technology of TiN/Cu superhard nanocomposite films prepared by multi-arc ion plating;
多弧离子镀制备TiN/Cu纳米复合超硬膜的工艺研究
5) multi-arc ion coating
多弧离子镀
1.
Effect of plasma parameters on thin film deposition during multi-arc ion coating;
多弧离子镀沉积过程中等离子体参数对薄膜沉积的影响
2.
Study on light absorption properties of nitrogen-doped titanium dioxide thin films prepared by multi-arc ion coating;
多弧离子镀镀制掺氮二氧化钛薄膜及其光吸收特性的研究
6) multi-arc ion-plating
多弧离子镀
1.
Anticorrosivity of Ti-Cr-N films deposited on ZL201 aluminum alloy by multi-arc ion-plating;
ZL201铝合金多弧离子镀涂层的耐腐蚀性能的研究
2.
Ti(C,N)-based cermets were coated with a TiN/TiAlN coating using multi-arc ion-plating technology.
采用多弧离子镀技术在Ti(C,N)基金属陶瓷基体上沉积了TiN/TiAIN涂层,通过扫描电镜、能谱仪、X射线衍射仪、原子力显微镜等分析技术对其显微组织、成分、相结构、粗糙度及涂层与基体间的结合强度进行了分析。
3.
The structure and phase of nickel films deposited by the multi-arc ion-plating on ZL201 aluminum alloy were analyzed by SEM and XRD.
用多弧离子镀的方法在ZL201铝合金表面制备了一层镍涂层,并用扫描电镜和X射线衍射仪对涂层表面形貌和物相进行了分析,结果表明:涂层表面存在着大量宏观颗粒,镍涂层呈现(200)晶面择优取向。