1) grafted membrane
接枝膜
1.
The machanical strength,resistance rate,expansion rate in alkaline electrolyte and alkaline absorbance of polyethylene-MAA grafted membrane were reported.
介绍了采用高压聚乙烯薄膜经γ射线辐照,然后在70℃的30%甲基丙烯酸的甲苯溶液中反应接枝的制备方法;报导了聚乙烯-MAA接枝膜的机械强度、电阻率、在碱液中的膨胀度以及吸碱液率等性能。
2) Binary monomers-grafted films
二元接枝膜
1.
Binary monomers-grafted films with temperature-and pH-sensitivities were prepared by photo-grafting of N,N-diethyl-acrylamide and acrylic acid onto polypropylene films with benzophenone(BP) as an initiator.
以二苯甲酮为引发剂,聚丙烯薄膜(CPP)为基材,通过紫外光接枝的方法制备了具有温度和pH值双重敏感特性的聚N,N-二乙基丙烯酰胺(PNDEA)与聚丙烯酸(PAA)二元接枝膜。
3) end grafted polymer films
端接枝聚合物膜
1.
The surface initiated polymerization and its use for the formation of end grafted polymer films were reviewed.
本文综述了无机物表面引发聚合反应用于制备高键合密度端接枝聚合物膜的研究进展 ,并对其今后的发展提出了见
4) humidity sensor of grafted film
接枝膜湿敏元件
5) surface photografting of LDPE film
LDPE膜表面光接枝
6) PE-AA grafted membrane
聚乙烯-丙烯酸接枝膜
1.
If there were much residual antioxidant and acrylic acid remained on the PE-AA grafted membrane,in a high humidity environment,the membrane would absorb moisture.
聚乙烯-丙烯酸接枝膜上的抗氧化剂和丙烯酸残留量较大时,在湿度较大的环境内隔膜吸收水分;抗氧化剂会破坏水化纤维素膜的大分子结构,使其抗拉强度降低,使锌银蓄电池的使用寿命缩短。
补充资料：表面接枝
分子式：
CAS号：
性质：液相单体在固态聚合物表面上进行的非均相接枝反应。用于聚合物膜、纤维及其他聚合物材料表面的改性。引发接枝的方法有：在固体聚合物表面含有还原性基团时，在氧化性引发剂存在下经氧化还原引发；辐照引发；等离子体引发等。用于天然及合成高聚物的改性，如纤维素纤维、淀粉、羊毛和蚕丝等的接枝改性。
CAS号：
性质：液相单体在固态聚合物表面上进行的非均相接枝反应。用于聚合物膜、纤维及其他聚合物材料表面的改性。引发接枝的方法有：在固体聚合物表面含有还原性基团时，在氧化性引发剂存在下经氧化还原引发；辐照引发；等离子体引发等。用于天然及合成高聚物的改性，如纤维素纤维、淀粉、羊毛和蚕丝等的接枝改性。