1) Molybdenum Alloy Piercing-Mandrel
钼合金顶头
2) Mo ejector
钼顶头
1.
Based on TZC material for PIM Mo ejector,study and on the site tests were made in respect of the high temperature strength and hardness and microscopic structures of the TZC alloy with the addition of single RE cerium and also Ce Yt RE element.
粉冶态钼顶头在TZC材质的基础上 ,通过添加单一稀土铈、钇和同时添加铈钇稀土元素 ,对其高温强度、硬度和金相组织等进行了研究及现场穿孔试验。
3) Sintered molybdenum piercing heads
粉冶钼顶头
4) ferromolybdenum
[,ferəumɔ'libdinəm]
钼铁合金
1.
The oxidizing roast of high impurity ferromolybdenum was studied by using rotary kiln.
采用回转窑加热的方法对高杂质钼铁合金氧化焙烧进行了研究。
2.
The ferromolybdenum(FeMo70)produced is in conformity to GB3649-87 standard.
通过试验获得了钼回收率与各影响因素之间的关系，冶炼出了符合ＧＢ３６４９－８７ＦｅＭｏ７０的钼铁合金，稳定试验时钼的回收率平均为９８。
5) Mo-Nb alloy
钼-铌合金
1.
Influences of vacuum (or residual pressure) in the melting chamber, chemical composition and specifications of Mo-Nb alloy feedstock bar, growing rate, rotation rate on processing Mo-Nb alloy single crystal have been discussed in detail.
主要讨论了熔炼室真空度,钼-铌合金原料棒化学成分和尺寸规格,熔炼速度,搅拌速度等对单晶制备的影响。
6) Mo-La_2O_3 alloy
钼镧合金
1.
A sort of Mo-La_2O_3 alloy strengthened with lanthanon's dispersion was gained by adopting a special preparation method to have the forerunner powder and one adulteration way of liquid & solid.
采用特殊制备前驱粉和液-固掺杂方式制备出弥散强化稀土钼镧合金,通过扫描电镜和透射电镜,研究了掺杂方式对钼镧合金烧结体中第二相的粒度分布和形貌,证实了钼基体中La2O3颗粒的存在,分析了第二相粒子在钼基体中的分布规律,测定了钼丝的拉伸性能,根据奥洛万机制,引入位错可滑移宽度的概念,分析了粒子尺度对材料硬化性能的影响,提出了改进小尺度第二相粒子强化钼合金加工性能的建议。
补充资料：钯钼合金
分子式：
CAS号：
性质：是钯基含钼的二元合金，包晶反应生成ε相，钼在钯（а相）中的溶解度最大可达40%。有PdMo5和PdMo10等合金。PdMo10合金的抗拉强度、布氏硬度和伸长率分别为549MPa，1255MPa和15%；硬状态下分别为1343.5MPa,2696.8MPa和2%。电阻系数90×10-2Ω·㎜2/m。含10%～25%Mo的合金可用高频炉熔炼，铸锭经旋锻成棒材。主要用作电阻材料。
CAS号：
性质：是钯基含钼的二元合金，包晶反应生成ε相，钼在钯（а相）中的溶解度最大可达40%。有PdMo5和PdMo10等合金。PdMo10合金的抗拉强度、布氏硬度和伸长率分别为549MPa，1255MPa和15%；硬状态下分别为1343.5MPa,2696.8MPa和2%。电阻系数90×10-2Ω·㎜2/m。含10%～25%Mo的合金可用高频炉熔炼，铸锭经旋锻成棒材。主要用作电阻材料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。