1) Fe/Al compound thin films
Fe/Al混合膜
1.
Fe/Al compound thin films were fabricated by pulse laser deposition(PLD) and its X-ray photon electron spectroscopy(XPS) examinations were conducted.
采用脉冲激光气相沉积(PLD)技术制备了Fe/Al 混合膜,测量了该混合膜的光电子能谱(XPS),并采用原子力显微镜(AFM)、扫描电子显微镜(SEM)对Fe/Al混合膜作了表面分析。
2) Fe/Al alloy thin films
Fe/Al合金薄膜
1.
In this paper Fe/Al alloy thin films were fabricated by pulse laser deposition(PLD),and the crystal phase,structure and micro-strain were studied.
采用PLD方法制备了Fe/Al合金薄膜,研究了Fe/Al合金薄膜的物相、结构、应力等。
3) Al-Fe alloy films
Al-Fe合金薄膜
4) Fe/Al powder
Fe/Al元素混合粉末
5) Al-Fe alloy
Al-Fe合金
1.
To investigate the effect of an alternating magnetic field on the morphology and distribution of iron-containing intermetallic phases in Al-Fe alloy,the near eutectic Al-1.
研究了交流磁场对Al-Fe合金中含铁相形态及分布的影响。
2.
In order to solve the problems of the primary Fe-rich phase separating the metal matrix seriously and deteriorating the property of hypereutectic Al-Fe alloy, rare earth (Y) metal was used to modify Al-5%Fe alloy.
针对普通熔铸条件下过共晶Al-Fe合金中初生富铁相严重割裂基体、恶化合金性能的问题,采用稀土元素Y对Al-5%Fe合金进行变质处理。
6) Fe-Al alloy
Fe-Al合金
1.
Positron lifetime measurements have been performed in binary Fe-Al alloys with different compositions and Fe3Al alloys doped with Cr and Si.
对二元Fe-Al合金,含Cr和Si的Fe3Al合金的正电子寿命谱侧量表明:随着二元 Fe-Al合金Al含量的增加,空位浓度增加,微孔洞的开空间增大,在Al含量高于40%(原子分数)的 B2-FeAl合金中存在着较高的空位浓度和开空间相当于Fe中10-15个空位聚集体的微空洞,在B3-FeAl和D03-Fe3Al合金中,晶格中最邻近的Fe－Al原子对之间发生Fe d-Alp杂化作用,Al的3p电子与Fe的3d电子被局域化并形成共价键,导致合金中的自由电子密度降低,二元Fe-Al合金中的平均电子密度随着Al含量的增加而下降,用Cr元素对Fe3Al进行合金化,合金基体和晶界处的自由电子密度均增加;而加入Si元素,合金基体和晶界处的自由电子密度均减小,讨论了Fe-Al合金的微结构对其力学性能的影响。
2.
The microdefect,electron density and the Fe 3d-Al 3p interaction in binary Fe-Al alloys with difference chemical composition have been investigated by positron lifetime spectra and coincidence Doppler broadening spectra of positron annihilation radiation.
采用符合正电子湮没辐射多普勒展宽装置和寿命谱仪研究不同化学成分的二元Fe-Al合金中的微观缺陷、电子密度以及Fe 3d-Al 3p电子的交互作用,合金元素对Fe-Al合金中微观缺陷、电子密度和3d电子的影响。
3.
Aluminum in molten zinc tends to segregate at the Fe:molten zinc interface with eventual precipitation of the Fe-Al alloy that inhibits the development of Fe-Zn compound.
从更微观的角度看,由于缺陷处浸入锌液后生成的Fe-Al合金层比正常部位少,抑制作用减小使该处合金化速度变快,所以缺陷处Zn-Fe合金层生成量大,容易产生条状凸起。
补充资料：Au-Pd-Cr-Pt-Fe-Al-Y alloys
分子式：
CAS号：
性质：金基与钯、铬、铂、铁、铝和钇的多元合金，电阻系数最高。生产方法参见金钯铬合金。可用作高温应变材料。
CAS号：
性质：金基与钯、铬、铂、铁、铝和钇的多元合金，电阻系数最高。生产方法参见金钯铬合金。可用作高温应变材料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条