1) direct wet chemical method
直接湿化学法
1.
A series of BaZr_xTi_1-xO_3 solid solutions were synthesized by means of direct wet chemical method at 95 ℃.
在95℃下用直接湿化学法,合成了系列BaTi1-xZrxO3固溶体粉体,XRD物相分析表明,产品为完全互溶取代固溶体,SEM和AFM观察,粒子为均匀球形,粒径大约为250 nm,BZT固溶体晶相均为立方相。
2) direct wet method
直接湿法
1.
On the basis of improving the fabrication process of in-direct wet method, the β-Li3TaO4 ceramic pebbles with small diameter of 0.
本文在改进间接湿法制备工艺的基础上,采用直接湿法制备了直径为0。
3) wet direct method
湿式直接法
4) wet chemical methods
湿化学法
1.
Research progress in preparation of quasi one-dimensional nanosized materials by wet chemical methods;
湿化学法制备准一维纳米材料的研究进展
2.
Comparing with the conventional ones,WO3 nano-powder prepared by wet chemical methods is thinner and more on the control of distribution of grain degree,and it’s with good uniformity and dispersivity.
综述了目前国内外湿化学法制备纳米WO3粉体的主要方法:水解法、沉淀法、溶胶-凝胶法、水热合成法及微乳液法,并对各种制备方法的优缺点进行了简要的讨论。
5) wet chemical method
湿化学法
1.
Synthesis and performance of chromium-doped spinel lithium manganese oxide prepared by wet chemical method;
掺铬锂锰氧化物的湿化学法合成与性能
2.
The optically variable pigments were produced by wet chemical method,and mica titanium having interference colors acted as host materials.
采用具有干涉色的云母钛作为基质材料,通过湿化学法制备随角异色功能颜料。
3.
4))O_3 porcelain powder is prepared by wet chemical method and it is characterized by X-ray Diffraction(XRD),infrared( IR),transmission electronic microscope(TEM).
针对微波介质瓷料系统成瓷过程中介电损耗较大且成瓷温度较高的问题,采用湿化学法制备(Ag0。
6) wet-chemical method
湿化学法
1.
Nanocrystalline YAG powders and translucent ceramics by wet-chemical method;
湿化学法合成YAG纳米粉体及透明陶瓷
2.
Nanocrystalline α-Al2O3 powder was prepared by a wet-chemical method calcining the dry NH4Al(OH)2CO3 precursor synthesized from NH4Al(SO4)2 and NH4HCO3.
以湿化学法制备的纳米α-Al_2O_3粉体作为添加剂,MgO和SiO_2为烧结助剂,对商用γ-Al_2O_3粉体预处理后,采用无压烧结工艺,有效的降低了烧结温度。
3.
(Luoyang Institute of Refractories Research, Ministry of Metallurgical Industry) ABSTRACT Sb_1O_3-doped SnO_2 semiconductor ceramics was prepared by means of wet-chemical method and thick film technology and its ethanol-sensing characteristics were measured.
采用湿化学法和厚膜技术制备了掺Sb_2O_2的SnO_2半导体陶瓷以测试其酒敏特性。