1) fluidity of grout
浆液流动度
2) fluidity of cement paste
净浆流动度
1.
Structure of superplasticizer was characterized by IR and effects of the product on fluidity of cement paste and water reduction for concrete were investigated.
利用IR表征了其结构,并考察了产品对水泥净浆流动度和混凝土减水率的影响。
2.
By means of orthogonal tests, fluidity of cement paste was used as main index to obtain optimum proportionof raw materials: AA:MMA:p-VBS = 1.
通过正交试验,以净浆流动度为主要指标,分析得出了原料的最佳配比AA∶MMA∶p-VBS=1。
3.
Influences of initiator,sulphonate,acrylic acid and diethylmaleate on fluidity of cement paste were studied in detailsAddition of diethyl maleate helped to reduce slump loss.
详细研究了引发剂、磺酸盐、丙烯酸和马来酸二乙酯等因素对净浆流动度的影响;马来酸二乙酯的加入,减小了流动度损失。
3) fluidity
[英][flu'ɪdəti] [美][flu'ɪdətɪ]
净浆流动度
1.
Researched the proportions of MAS、PEO、AA on the fluidity of cement and the gradual loss to determine the dispersing mechanism mainly are electyostatic repulsion force,steric stability,there also is slow release of macromelocule.
在合成聚羧酸系高效减水剂时,不同单体MAS、PEO、AA的加入量对减水剂的性能有不同的影响,主要是由于各个功能单体对水泥颗粒的分散机理不同,通过研究MAS、PEO、AA的加入量对水泥净浆流动度的影响,从而确立了其在水泥中的作用机理主要是静电斥力,空间位阻,此外还有反应性高分子缓慢释放理论,这对于指导聚羧酸系高效减水剂的合成具有很大的参考价值。
2.
The initial fluidity of the cement pas.
以初始净浆流动度为考察指标,通过正交和单因素实验,确定合成聚羧酸系水泥减水剂的最佳工艺条件:APS用量为0。
3.
The initial fluidity of the cem.
以初始净浆流动度为考察指标,通过正交和单因数实验确定合成聚羧酸系水泥减水剂的产品配方(APS,0。
4) cement paste fluidity
净浆流动度
1.
Correlativity test of cement paste fluidity and concrete rheologic property;
水泥净浆流动度与混凝土流变性能相关性试验
2.
The results showed that the saturation content of water reducer could be determined according to mortar dispersion degree rather than cement paste fluidity.
5水泥和3种减水剂,分别检测了不同减水剂掺量时水泥净浆流动度和胶砂扩展度,结果表明,根据胶砂扩展度可以明显地确认减水剂的饱和掺量,而根据水泥净浆流动度较难确认。
3.
The dosage range corresponding to the saltation of SPs fit well with the saturation point measured by cement paste fluidity.
结果发现,当减水剂掺量达某范围,分形维数出现突变,突变处对应的减水剂掺量与净浆流动度测定减水剂饱和掺量吻合良好。
5) slurry flow properties
浆液的流动性能
6) cement paste fluidity
净浆流动度法
1.
Comparation between Marsh cone and cement paste fluidity to test adaptability of cement and water retarder;
Marsh筒法和净浆流动度法用于水泥与减水剂适应性测试的比较
补充资料：高化流动度试验仪
分子式：
CAS号：
性质：又称高化流动度试验仪，系日本高分子化学会定型的一种流动试验仪，属于柱塞加压式，毛细管挤出型。这种试验仪可适当选择负荷，自动记录柱塞下降量与时间的关系，并由此求出体积流速等流动特性。料筒温度在80～320℃范围内由电加热调节，并可以等速升温。负荷的选择范围为0.98～49.03MPa，通过改变负荷和毛细管的长径比，可获得较宽的剪切速率范围。这种定负荷式流动试验仪作为质量控制手段已得到广泛的应用。
CAS号：
性质：又称高化流动度试验仪，系日本高分子化学会定型的一种流动试验仪，属于柱塞加压式，毛细管挤出型。这种试验仪可适当选择负荷，自动记录柱塞下降量与时间的关系，并由此求出体积流速等流动特性。料筒温度在80～320℃范围内由电加热调节，并可以等速升温。负荷的选择范围为0.98～49.03MPa，通过改变负荷和毛细管的长径比，可获得较宽的剪切速率范围。这种定负荷式流动试验仪作为质量控制手段已得到广泛的应用。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条