1) Fe-79%Ni alloy
Fe-79%Ni
1.
Fe-79%Ni alloy was prepared by vacuum electric arc smelting and annealed at different temperatures for different times.
采用真空电弧炉熔炼Fe-79%Ni合金,经过不同的热处理工艺进行退火处理。
3) nanoscale Ni/Fe
纳米Ni/Fe
1.
Nanoscale iron and nanoscale Ni/Fe bimetal were used to dechlorinate carbon tetrachloride (CT).
反应进行 1h ,纳米Ni/Fe ,纳米Fe和铸铁屑的脱氯率分别为 98%,84 %和 6 5 %;纳米Ni/Fe和纳米Fe产生的中间产物三氯甲烷 (TCM)最大量分别为 2 5 %和 5 9%,随之TCM又逐渐下降 ,尤其是纳米Ni/Fe在很短时间内 ,将TCM快速完全脱氯且产生 2 7%甲烷 (CH4)和 1 5 %二氯甲烷 (DCM) ,并对DCM没有明显的脱氯作用。
2.
Nanoscale Ni/Fe Were prepared adopting chemical precipitation technique, and studies on catalytic dechlorination of Polychlorinated Biphenyls using the prepared nanoscale Ni/Fe were carried out in this paper.
本文采用化学沉淀法制备纳米Ni/Fe双金属颗粒,利用制备的纳米Ni/Fe对PCBs进行还原降解研究。
4) Fe-Ni film
Fe-Ni薄膜
5) Ni-Fe alloy
Ni-Fe合金
1.
Electrochemical behaviors of Ni-Fe alloy codeposition;
Ni-Fe合金共沉积的电化学行为
2.
Progress of Ni-Fe alloy plating;
Ni-Fe合金电镀的研究进展
3.
Corrosion resistance and destruct process of Ni-Fe alloy coatings by electrodeposition were studied by weight loss,anodic polarization curve and EIS techniques.
本文采用失重、阳极极化和电化学阻抗谱等方法研究了电沉积Ni-Fe合金镀层腐蚀性能和镀层的破坏过程。
6) (Fe,Ni)_3V
(Fe,Ni)3V
补充资料：W-Ni-Fe alloy
分子式：
CAS号：
性质：一类重要的钨基重合金。它们是在钨中添加镍、铁而组成的合金，以及在这个基础上再加入其他金属元素的合金。加入的镍铁比一般为7：3或1：1。这类合金应用极广，已经成为用量最大的主要钨基重合金。其特点是烧结密度高，强度与塑性均较好，有一定的铁磁性。合金作为一般应用，如配重、平衡锤、防辐射屏蔽装置等，都直接使用烧结合金；但如作为要求高机械性能的应用时，合金则需变形加工及热处理以达到强化。
CAS号：
性质：一类重要的钨基重合金。它们是在钨中添加镍、铁而组成的合金，以及在这个基础上再加入其他金属元素的合金。加入的镍铁比一般为7：3或1：1。这类合金应用极广，已经成为用量最大的主要钨基重合金。其特点是烧结密度高，强度与塑性均较好，有一定的铁磁性。合金作为一般应用，如配重、平衡锤、防辐射屏蔽装置等，都直接使用烧结合金；但如作为要求高机械性能的应用时，合金则需变形加工及热处理以达到强化。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。