1) corrosion thermal fatigue
腐蚀性热疲劳
1.
2 boilers in Ningxia Dawukou Power Plant, points out that the failure of water-cooling wall tubes is due to the factors of vibration during the start and stop of the boiler and the high sulfur in coal etc, results in the corrosion thermal fatigue on flue gas side, puts forward relevant counter measures.
通过对国电宁夏大武口发电厂#1、#2炉水冷壁管存在的横向裂纹现象进行宏观检验、化学分析、力学性能、金相显微组织分析,指出水冷壁管横向裂纹的主要原因是由于运行过程中存在启停振动、燃煤含硫量偏高等因素,导致水冷壁管在运行过程中产生烟气侧腐蚀性热疲劳。
2) Fatigue failure of hot corrosion
热腐蚀疲劳
3) corrosion and heat fatigue
腐蚀热疲劳
1.
It was concluded that it was corrosion and heat fatigue that caused the bursting.
通过对某电厂水冷壁爆管试样的宏观形貌、化学成分、显微组织、断口形貌等的分析,得出其发生爆管的主要原因是外界热冲击导致的腐蚀热疲劳。
4) corrosion fatigue properties
腐蚀疲劳性能
5) fatigue strength under corrosion for finite life
耐腐蚀疲劳性
6) corrosion fatigue
腐蚀疲劳
1.
Mechanism of corrosion fatigue for as-extruded magnesium alloy AZ80;
变形镁合金AZ80的腐蚀疲劳机理
2.
A Study on Corrosion Fatigue Behavior in High Strength Aluminum Alloy LC4CS;
LC4CS高强铝合金腐蚀疲劳行为研究
3.
Study on the law of fatigue stiffness decay of reinforced concrete beams subjected to corrosion fatigue;
混凝土梁腐蚀疲劳刚度衰减规律
补充资料：热疲劳
分子式：
CAS号：
性质：当容器或构件由于其温度的反复变化而引起其金属材料的疲劳现象称为热疲劳。
CAS号：
性质：当容器或构件由于其温度的反复变化而引起其金属材料的疲劳现象称为热疲劳。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。