1) durable hardness
持久硬度
1.
This paper deals with the high- temperature durable hardness and the creep under the condition of different stresses at 550t of 20Cr11Mo NbNB heat resisting steel.
本文研究了新型２０Ｃｒ１１ＭｏＶＮｂＮＢ耐热钢的高温持久硬度和５５０℃不同应力下的蠕变。
2) permanent hardness of water
永久硬度
3) rupture strength
持久强度
1.
A statistical analysis method based on Z-parameter to assess rupture strength of a high temperature steel is proposed,where parameter Z describes the degree of deviation of experimental data from the Larson-Miller curve.
提出一种基于Z参数的耐热钢高温持久强度可靠性分析方法。
2.
The paper explores the effect of the heat treatment temperature on the rupture strength of P91 steel welding joint.
探求了热处理温度对P91钢焊接接头持久强度的性能影响。
3.
A statistical analysis method based on Z-parameter to assess rupture strength of a high temperature steel is proposed,where parameter Z describes the degree of deviation of experimental data from the Larson-Miller curve.
提出一种基于 Z 参数的耐热钢高温持久强度可靠性分析方法。
4) creep rupture strength
持久强度
1.
Effect of Solution Heat Treatment on Creep Rupture Strength of Steel 1Cr19Ni11Nb;
固溶热处理对1Cr19Ni11Nb钢持久强度的影响
2.
Then,the creep rupture strength experiment at high temperature of 350 ℃ is carried out according to the GB6395-86 Metallic Materials Stress Rupture Testing at elevated temperature.
按GB6395-86《金属高温拉伸持久试验方法》标准规定对该合金进行了350℃下的持久强度试验。
3.
Low circle fatigue properties、fatigue crack propagation rates (at room temperature、550℃、575℃)、creep rupture strength (at 550℃、575℃) on weld joints of P91 pipe was investigated to study the temperature's influences on their behaviours.
测试了P91大口径钢管以及其焊接头在三个不同温度 (室温、5 5 0℃、5 75℃ )下的低周疲劳、疲劳裂纹扩展速率和 5 5 0℃、5 75℃持久强度 ,以研究分析温度对其低周疲劳特性、疲劳裂纹扩展、持久强度的影响 ,并了解焊接头与母材之间的差异。
5) sustained strength
持久强度
1.
The chemical composition, mechanical property, microstucture and sustained strength of T91 steel tube for 60.
3×8mm的T91钢管进行了化学成分、力学性能、金相组织、持久强度的试验,并对母材及手工氩弧焊接头的T91钢管进行了时效试验和时效后的力学性能、金相组织测定。
2.
The mechanical properties, serial impact and sustained strength of the welded joint aged at 650 ℃ for long-time of E911 steel produced by German Vallourec & Mannesmann were tested, optical microscope, transmission electron microscope (TEM) and scanning electron microscope (SEM) were used to observe and analyze the microstructures and the fracture apptarance.
对德国Vallourec & Mannesmann公司生产的E911钢焊接接头在650℃长期时效后进行了力学性能、系列冲击试验,并对E911钢焊接接头在650℃高温持久强度进行了测试。
3.
It is measured by this thesis that the chemical composition, mechanical property, microstructure and sustained strength of T23 steel tube.
本文对T23钢母材及焊接接头进行了力学性能、显微组织、持久强度的分析和试验，研究了T23钢母材及手工氩弧焊焊接接头的高温性能。
6) keeping precision
持久精度
补充资料：工程塑料硬度的检测--巴氏硬度计
HBa-1巴 氏 硬 度 计巴柯尔 (Barcol) 硬度 ( 简称巴氏硬度 ) 最早由美国 Barber-Colman 公司提出，是近代国际上广泛采用的一种硬度门 类，以特定压头在标准弹簧的压力作用下压入试样，以压痕的深浅表征试样的硬度。巴柯尔硬度计（巴氏硬度计）作为 专门测量玻璃钢制品、增强或非增强硬塑料、铝及铝合金、黄铜、紫铜等较软金属硬度的专用检测工具 （ 特别 适用于玻璃钢制品 ），已被大多数国家或国际组织认可。美国材料试验协会（ ASTM ）、日本工业规范（ JIS ）、中国等国家相继制定 《用巴柯尔硬度计测量玻璃钢（ GRP ）硬度试验方法》,《纤维增强塑料巴氏（巴柯尔）硬度试验方法》GB/T3854-1983 的国家标准。因此，巴柯尔硬度计是各生产单位、计量部门在质量认证、质量监控、计量测试等方面首选的专用检测仪器。 无锡市计量科学研究所，是我国制定巴柯尔硬度检定标准的主要参与者、巴柯尔硬度最高标准器的拥有者和国产第一台巴柯尔硬度计的研制和生产单位，也是国家实验室认证的巴柯尔硬度计专业检测机构。经过二十多年的不断完善，本所生产的 H Ba 系列巴柯尔硬度计的各项性能和技术指标完全与美国 Barber-colman 公司 GYZJ 系列硬度计相媲美 。