1) recycled coarse aggregate
再生粗集料
1.
An experimental study of high-temperature on it s influences to recycled coarse aggregate;
高温作用对再生粗集料性能影响的试验研究
2.
In this paper,a kind immersing-crystallizing material(ICM)is used to enhance the mechanical properties and durability of recycled coarse aggregate concrete(RCC)as the complicated interface zone structures is concerned.
针对再生粗集料混凝土的界面结构特征,设计采用掺加渗透结晶材料的措施改善其力学性能和耐久性。
3.
Regarding to the various sources of waste concrete, digital image processing technology was applied to analyze the relative content of mortar, attaching on the surface of recycled coarse aggregates with different max diameters.
针对废弃混凝土来源的多样性,采用数字图像处理方法分析了不同最大粒径再生粗集料砂浆组分的相对含量,最大粒径控制为20mm时能有效地减少砂浆组分的含量。
2) recycled coarse aggregate(RCA)
再生粗集料
1.
The gas anti-permeability and carbonation resistance of recycled concrete,which was prepared by using waste concrete as recycled coarse aggregate(RCA) and some cement and mineral additions as raw materials,were studied.
以废弃混凝土为再生粗集料,再适当掺加一定量的水泥和矿物掺和料,制成再生混凝土。
2.
The test results indicate that recycled coarse aggregate(RCA) replacement ratio and different water/cement (w/c) ratios have a great influence on SRC,in condition that the design flexural strength is 6.
结果表明:再生粗集料的含量和水灰比等因素对钢纤维再生混凝土的抗折强度影响较大,在设计抗折强度为6。
3) recycled coarse aggregate (RCA) replacement ratio
再生粗集料取代率
1.
The influence of different recycled coarse aggregate (RCA) replacement ratios on the strength of recycled concrete was investigated.
最后,针对再生粗集料取代率为100%的C20~C40再生混凝土主要强度指标的取值提出了建议。
4) recycled coarse aggregate concrete
再生粗集料混凝土
1.
Basic behaviors of recycled coarse aggregate concrete with fly ash;
粉煤灰再生粗集料混凝土基本性能研究
5) recycled coarse aggregate
再生粗骨料
1.
Experimental research on characteristic of recycled coarse aggregate after high-temperature;
高温作用后再生粗骨料特征性能试验研究
2.
Influence of particle shaping on the workability of recycled coarse aggregate concrete;
颗粒整形对再生粗骨料混凝土工作性的影响
3.
Basic properties of recycled coarse aggregate concrete by orthogonal analysis
正交法分析再生粗骨料混凝土的基本性能
6) recycled aggregate
再生粗骨料
1.
Based on geometrical characteristic of recycled aggregate and it s influence to the microscopic structural of recycled aggregate concrete,the thesis mainly analyzes the causes for lower durability of recycled aggregate concrete than common concrete.
基于再生粗骨料的几何特征及其对再生混凝土微观结构的影响,分析了再生混凝土耐久性较普通混凝土差的原因。
2.
The other factors are recycled aggregate,water cement ratio,high efficiency water reducing agent and fly ash.
采用再生粗骨料配制高强度混凝土,研究再生高强混凝土的抗拉性能。
补充资料：集料
用于配制混凝土或砂浆的颗粒状松散材料，也称骨料。在混凝土中，集料一般占体积的70～80％，主要起骨架作用，对混凝土的性能和技术经济指标都有很大的影响。集料分为粗集料和细集料两种,按中国的标准,颗粒粒径大于5毫米的称为粗集料，小于5毫米的称为细集料。按其容重不同，集料又可分为重集料、普通集料和轻集料三种，分别用于配制防辐射混凝土、普通混凝土和轻集料混凝土。此外，还有一些特殊用途的集料，如耐火集料、耐酸集料等。
普通集料大部分是?烊患希灿幸徊糠质枪ひ捣显希ㄈ缫苯鹪龋４旨贤ǔ剖樱幌讣贤ǔ粕白印０雌淅丛醇氨砻孀刺涌煞治槭⒙咽八槁咽簧白釉蚍治由啊⑸缴凹昂Ｉ啊８骼嗉嫌志云淞＞痘虼窒赋潭确旨丁?
集料的质量对所制成混凝土的性能影响很大。其中如粗、细集料的级配不良会使混凝土拌合物的和易性下降，水泥用量显著增加；粗集料中针、片状颗粒含量过多同样会影响混凝土拌合物的和易性，并导致高标号混凝土强度降低；集料含泥过高会使混凝土的强度、抗冻及抗渗性能明显下降；海砂中的氯盐含量过多会引起混凝土中钢筋锈蚀。使用前除要求对上述指标检验外，其他如碱-集料反应、坚固性、有机质及有害物质含量、强度等也应按需要进行检验。
集料的使用量很大，尤其是制作普通混凝土用的砂、石，全世界每年耗用数十亿立方米，不少地区的集料已经面临资源枯竭。因此,开发各种新的天然集料资源,研制各种人造集料和寻找合适的代用材料，已成为目前混凝土集料发展的重要任务。其中，如海砂及海卵石、工业废渣、二次集料等的应用，已取得较好效果。
普通集料大部分是?烊患希灿幸徊糠质枪ひ捣显希ㄈ缫苯鹪龋４旨贤ǔ剖樱幌讣贤ǔ粕白印０雌淅丛醇氨砻孀刺涌煞治槭⒙咽八槁咽簧白釉蚍治由啊⑸缴凹昂Ｉ啊８骼嗉嫌志云淞＞痘虼窒赋潭确旨丁?
集料的质量对所制成混凝土的性能影响很大。其中如粗、细集料的级配不良会使混凝土拌合物的和易性下降，水泥用量显著增加；粗集料中针、片状颗粒含量过多同样会影响混凝土拌合物的和易性，并导致高标号混凝土强度降低；集料含泥过高会使混凝土的强度、抗冻及抗渗性能明显下降；海砂中的氯盐含量过多会引起混凝土中钢筋锈蚀。使用前除要求对上述指标检验外，其他如碱-集料反应、坚固性、有机质及有害物质含量、强度等也应按需要进行检验。
集料的使用量很大，尤其是制作普通混凝土用的砂、石，全世界每年耗用数十亿立方米，不少地区的集料已经面临资源枯竭。因此,开发各种新的天然集料资源,研制各种人造集料和寻找合适的代用材料，已成为目前混凝土集料发展的重要任务。其中，如海砂及海卵石、工业废渣、二次集料等的应用，已取得较好效果。