1) Porous permeable bricks
多孔透水砖
1.
Porous permeable bricks were made with gold tailings as the main material and coal gangue as pore-forming agent.
以黄金尾矿为主要原料,以煤矸石作成孔剂,制备了多孔透水砖。
2) water permeable brick
透水砖
1.
Study on preparation of fly ash water permeable brick;
粉煤灰透水砖的制备研究
2.
With onvetion production technology water permeable brick with high added value is fabricated in low cost with damaged ceramics and ceramic wastes adding domestic wastes,and the effects of adding quantity of domestic wastes on sample performance are discussed.
添加生活垃圾利用陶瓷废料,在常规生产工艺下低成本制造高附加值的透水砖,探讨了生活垃圾添加量对砖性能的影响,提高生活垃圾添加量可以提高透水砖的抗折强度和致密度,但降低了砖的透水性能和吸水率。
3.
The results showed that the optimal firing temperature of water permeable brick was at 1 100 ℃ for 1 h.
以废陶瓷为主要原料,成功地制备了透水性能好、强度高的透水砖样品。
3) pervious brick
透水砖
1.
Investigation of effect of polymer on properties of ecotype pervious brick;
聚合物对生态透水砖性能影响的研究
2.
Research on the performance of pervious brick used in urban road;
城市道路用透水砖性能研究
3.
Influence of raw material particle size,body formula,molding and sintering system on the mechanical properties,porosity,permeability coefficient and average pore size of porous pervious brick using ceramic waste as main material was analyzed to provide a new alternative for the use of ceramic waste.
分析了原料的颗粒大小、配方、成型压力和烧成制度等对以陶瓷废料为主要原料的多孔透水砖的力学性能、气孔率、平均孔径和透水系数等的影响,为陶瓷废料的利用开辟了一条新途径。
4) permeable bricks
透水砖
1.
Making and functional test of burning-free permeable bricks;
免烧透水砖的制作与性能测试
2.
The Research of the Fly-ash Physicochemical Property and the Fly-ash Preparation Permeable Bricks;
粉煤灰理化性质分析及粉煤灰透水砖的制备研究
5) porous pervious concrete
多孔透水混凝土
1.
Effects of some factors such as gradation and particle size of aggregate,mass ratio of aggregate to cement,mass ratio of water to cement,admixtures and mixing process on the properties of porous pervious concrete(PPC) including porosity,permeation coefficient and compressive strength were studied.
研究了若干因素如骨料级配与粒径、骨灰比、水灰比、外加剂及搅拌工艺等对多孔透水混凝土的空隙率、透水系数与抗压强度等性能的影响。
6) Porous stone
透水石、多孔石
补充资料：为特型耐火砖和特异型砖
分子式：
CAS号：
性质：又称为特型耐火砖和特异型砖。是一类外形特别复杂的耐火砖。中国标准规定，对于黏土质、高铝质特异型耐火砖，其外形尺寸的比例(最小与最大尺寸之比)在1:8范围以内；厚度尺寸为35～135mm，或管状砖的长度尺寸不大于300mm；具有不多于4个凹角(包括圆弧状凹角在内)，或具有1个30°～50°的锐角，或带有不多于8个沟槽，或有不多于1个孔眼。黏土质耐火砖重1.5～30kg；高铝质耐火砖重1.5～35kg。硅质特异型耐火砖，其外形尺寸的比例在1:6范围以内，厚度尺寸为35～135mm，或管状砖的长度尺寸不大于300mm；具有不多于4个凹角(包括圆弧状凹角在内)，或具有30°～50°的锐角，或带有4个沟槽，或带有不多于1个孔眼，重1.5～25kg。
CAS号：
性质：又称为特型耐火砖和特异型砖。是一类外形特别复杂的耐火砖。中国标准规定，对于黏土质、高铝质特异型耐火砖，其外形尺寸的比例(最小与最大尺寸之比)在1:8范围以内；厚度尺寸为35～135mm，或管状砖的长度尺寸不大于300mm；具有不多于4个凹角(包括圆弧状凹角在内)，或具有1个30°～50°的锐角，或带有不多于8个沟槽，或有不多于1个孔眼。黏土质耐火砖重1.5～30kg；高铝质耐火砖重1.5～35kg。硅质特异型耐火砖，其外形尺寸的比例在1:6范围以内，厚度尺寸为35～135mm，或管状砖的长度尺寸不大于300mm；具有不多于4个凹角(包括圆弧状凹角在内)，或具有30°～50°的锐角，或带有4个沟槽，或带有不多于1个孔眼，重1.5～25kg。