1) strip casting
鳞片铸锭
1.
A high performance sintered NdFeB magnet with N52 was prepared by strip casting, hydrogen decrepitation, jet milling, rubber isostatic pressing with impulse magnetic field and vibrating.
采用鳞片铸锭、氢爆加气流磨制粉、脉冲场振动取向加橡皮模等静压成型等改进的技术在工业生产线上成功制造了N52高性能烧结NdFeB磁体。
2.
05(C) ingots by strip casting has been systematically investigated by SEM.
05(简称C合金)鳞片铸锭。
2) ingot
[英]['ɪŋɡət] [美]['ɪŋgət]
铸锭
1.
Effect of ultrasonically melt treatment method on solidification structure of pure aluminum ingot;
超声波熔体处理方法对纯铝铸锭凝固组织的影响
2.
Research on Bulky Compound of 7A52 Alloy Ingot under Funnel;
7A52合金铸锭漏斗底结物形成原因
3.
Effects of 5083 aluminium alloy ingot homogenizing on properties and structures of ingot and plates;
5083铝合金铸锭均匀化处理对铸锭和板材组织与性能的影响
3) ingots
铸锭
1.
Effects of Melt Treatment Methods on Degassing Efficiency of Ultrasonically Refined Al-1.65%Si ingots Under Different Ultrasonic Frequencies;
不同超声波频率下熔体处理方法对Al-1.65%Si铸锭除气的影响
2.
Effect of Ultrasonic on Structure of Aluminum Alloy Ingots;
超声波对铝合金铸锭组织的影响
3.
In this study,the effect of ultrasonic treatment time on crystallization structure of industry pure aluminum ingots was investigated.
研究了超声波处理时间对工业纯铝铸锭结晶组织的影响,即添加除气剂又进行超声波处理的情况。
5) Casting
[英]['kɑ:stɪŋ] [美]['kæstɪŋ]
铸锭
1.
5 alloys during both copper mold casting and melt-spinning were studied.
5两种合金铸锭的非平衡凝固过程及组织、快淬速度对薄带相结构的影响进行了研究。
2.
In the fields of NdFeB sintering, casting and HDDR technique, the superconducting magnet has been used and showed excellent results.
概述了超导磁体技术的研究进展,分析了超导磁体在NdFeB永磁材料制备过程中的应用前景,重点讨论了超导磁体在烧结NdFeB磁体、NdFeB铸锭组织、HDDR(氢化-歧化)工艺制备NdFeB纳米晶粉末等领域的具体应用情况。
6) ingot casting
铸锭
1.
Research on coarse compound in 7A52 alloy ingot casting
7A52合金铸锭粗大化合物研究
2.
A modified process for ingot casting was put forward which adjusted the meting current and the melt- ing rate leading to effective improving iron segregation in Ti-1023 alloy.
根据凝固理论论述了 Ti-1023合金中的宏观及微观 Fe 元素偏析存在的原因,对铸锭生产中熔化电流、熔化速度提出切实可行的工艺方案,有效地改善 Ti-1023合金的熔炼偏析。
补充资料：生铁模铸锭
生铁模铸锭
iron mould casting
shengtlemu Zhudlng生铁模铸锭(iron mould easting)将熔体注入生铁模型铸造锐坯的工艺方法。生铁模铸锭是有色金属合金铸锭生产最常用、最简单的一种铸锭方式。由于方法简单、灵活以及投资少等特点，在中、小型企业中广泛应用。生铁模和在生铁模基础上发展起来的水冷生铁模铸锭，按浇注方式划分有水平锭模铸锭、垂直锭模铸锭和倾动锭模铸锭;按锭模结构划分，在垂直锭模铸锭中还分整体式锭模铸锭和对开式锭模铸锭。 水平锭模铸锭生产像铅、锡类的低熔点金属合金以及对铸锭表面和内部组织无严格要求、不直接用于塑性加工的铸坯，如中间合金铸块、各种废料和回炉重熔的铸块等。 垂直锭模铸锭用于铜及铜合金锭坯生产。垂直锭模分整体式和对开式两种口整体式垂直锭模用于圆柱形断面铸坯生产，为了脱模方便，模内壁加工成一定锥度。这种锭模铸锭几何尺寸稳定、铸翅少，但不适于径高比小和凝固收缩率小的铸坯生产。对开式垂直锭模与整体式垂直锭模相比，更有利于模子内壁的清理和润滑，也易于脱模，但这种锭模铸锭易产生铸翅和变形。不论整体式还是对开式的垂直锭模都可以在模壁外侧安装水套做成水冷生铁模。 倾动式锭模铸锭常用于铝及铝合金板坯生产。浇注过程中锭模能围绕模子重心的水平轴，平稳地倾少 倾动模铸锭浇注过程示意图 1一浇包;2一金属液体流;3一金属模;4一模座动一定的角度，使液流沿锭模侧边稳定地流入模底(见图)。液流的表面氧化膜受到保护，液流在模内也不产生激烈的翻腾和搅动。 倾动模铸锭能有效地减少氧化损失和防止产生因液体金属的机械运动而带入的金属氧化夹渣和过量的有害气体所造成的铸锭缺陷。 (郎振旗)