1) independent melting
共晶组织分层熔化
2) eutectic melting
共晶熔化
3) Eutectic structure
共晶组织
1.
Effects of Cooling Rate on Eutectic Structure of Zn-0.24Ni Alloy;
冷却速度对Zn-0.24Ni合金共晶组织的影响
2.
Effects of neodymium and cooling rate on eutectic structure in AZ91HP magnesium alloy
Nd与冷却速度对AZ91HP镁合金共晶组织形貌的影响
3.
Besides,microscopic structure is eutectic structure of γ-.
结果表明:该涂层与基体呈冶金结合,内部组织均匀细密无缺陷,是固溶了大量Cr的-γFe相与高硬度析出相的共晶组织;其在海水中的耐蚀性远高于0Cr18Ni9Ti不锈钢,两者在海水中均表现为点蚀。
4) eutectic microstructure
共晶组织
1.
By means of analysis of solidification process of eutectic microstructure, it is shown that the “high affinity between Sn and RE” leads to the change of contact angle at the three phase junction of S/L interface.
通过对共晶组织凝固过程的分析 ,发现稀土元素的“亲Sn”现象导致固液界面处三相交汇点接触角的变化 ,并最终促使共晶组织直接在先析出富Pb相上生长 ,从而抑制了原始组织中粗大的富Sn相晕圈的出现 ,实现了金相组织的均匀化。
2.
The results show that,with Al content increasing,primary phaseα-Mg in as-cast Mg-Al binary alloy decreases,while eutectic microstructure severely increases.
结果表明:铸态Mg-Al二元合金在含Al(10%～25%,质量分数,下同)范围内,随Al含量增加,α-Mg初晶体积分数逐渐减少,形态由不规则的团絮状变为蔷薇花状,直至小块状;共晶组织体积分数剧增,硬脆相β-Mg17Al12呈网状连续分布,α和β两相以共生生长方式成为片层状共晶组织;ECAP能明显破坏硬脆相β-Mg17Al12网状连续分布,细化共晶组织和初晶α,并能使初晶α中析出弥散细小的β,起到弥散强化作用,使不同Al含量的Mg-Al二元合金不仅抗拉强度得到显著提高,而且塑性获得极大改善,尤其是Mg-15Al合金,ECAP后抗拉强度σb从150MPa提高到269。
6) eutectic structure rate
共晶组织率
1.
Cast tungsten carbide produced by new nethod featuresstable carbon content,high eutectic structure rate, small eutectic size, low porosity rate, high density and hardness,good wearresistance and long service life.
新方法生产的铸造碳化钨具有碳含量波动小、共晶组织率高、共晶尺寸小、孔隙率低、密度大、硬度高、耐磨性好和使用寿命长等优点。
补充资料：共晶组织
eutecticstructure：完全由共晶体所组成的组织。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。