1) spli-(tting) tensile bonding strength
劈拉粘结强度
2) adhesive splitting tensile strength
粘结劈拉强度
1.
The test results show that the splitting section arises in the adhesive section of polymer mortar and concrete,and the adhesive splitting tensile strength increases with the increasing of concrete strength.
进行了砂浆和不同强度混凝土的粘结劈拉试验,试验结果表明,聚合砂浆与混凝土之间的劈拉破坏为粘结面破坏,粘结劈拉强度随混凝土强度的增大而增大。
3) splitting tensile strength
劈拉强度
1.
Experimental research on the splitting tensile strength for joint surface of concrete construction joint;
混凝土施工缝接缝面劈拉强度试验研究
2.
Experimental study on the splitting tensile strength for joint surface of construction joint;
施工缝粘结面劈拉强度试验研究
3.
Experimental research on bond splitting tensile strength of new-old concrete after high temperature;
混凝土高温后进行粘结劈拉强度试验研究
4) splitting strength
劈拉强度
1.
The main objective of the tests is to determine the relationship between the tensile strength and splitting strength of steel fiber reinforced concrete(SFRC).
分析研究了钢纤维高强混凝土的轴拉强度和劈拉强度的关系,钢纤维高强混凝土轴拉性能随钢纤维体积掺量、基体强度及钢纤维类型的变化规律。
2.
The workability of fresh concrete and the compressive strength,splitting strength,flexural strength,elastic modulus and poissson ratio at different ages are measured and analyzed.
测量了新拌混凝土的工作性能,及不同龄期的抗压强度、轴心抗压强度、劈拉强度、抗折强度、弹性模量及泊松比,对这些基本力学参数进行了分析比较,总结了随龄期的发展规律,并与同配比振捣混凝土进行了比较,为设计自密实混凝土提供了依据。
3.
The relationship between cylinder strength and splitting strength, cylinder strength and elastic m.
随后,作者通过试验的方法对自密实混凝土的基本力学性能做了研究,并比较了圆柱体抗压强度与劈拉强度、圆柱体抗压强度与弹性模量以及三者与混凝土密度之间的关系。
5) tensile strength
劈拉强度
1.
The influence of HPP fiber on the compression strength,tensile strength and apparent density of light-aggregate concrete was also studied.
并通过试验研究了高性能异型塑钢纤维(HPP)对轻骨料混凝土抗压强度、抗劈拉强度以及表观密度的影响,研究表明,不同掺量的HPP纤维对轻骨料混凝土的表观密度、抗压强度没有显著影响,但能明显改善轻骨料混凝土的抗拉性能。
2.
The tensile strengths of saturated and dry concrete under different loading rates were studied by splitting tensile tests.
利用大型液压伺服试验机研究了不同加载速率下饱和混凝土与干燥混凝土的劈拉强度变化情况,试验研究表明:在准静态加载时,与干燥的混凝土相比饱和混凝土的劈拉强度有所降低,随着加载速率的升高,饱和混凝土的的动态劈拉强度有较大的提高。
3.
By the study on the carbon fibre reinforced cement, this paper finds the relations between carbon fibre contemt and composites compressive strength and tensile strength.
本文通过对水泥基体掺入碳纤维进行研究，得出了复合体抗压强度、劈拉强度与碳纤维掺量的关系。
6) cleavage strength
劈拉强度
1.
A study on adherence cleavage strength of new and old concrete;
新老混凝土粘结劈拉强度试验研究
2.
With raw materials of Jinping first-level hydropower station,the experimental study on performance of hydraulic concrete with magnesia shows that the compressive strength of concrete added with magnesia is descreased slightly and cleavage strength,tensile strength,modulus of elasticity,tensile strain ultimate of concrete added with magnesia are increased slightly.
通过采用锦屏一级水电站的原材料,对外掺氧化镁的水工混凝土性能试验研究表明,外掺氧化镁对混凝土的抗压强度略有降低,对劈拉强度、轴拉强度、弹性模量、极限拉伸值略有提高;未掺氧化镁的砂岩混凝土180d自身体积变形为-57。
补充资料：粘结强度
粘结强度
bonding strength
n janjje qjangdu粘结强度(bonding strength)两种材料粘结在一起时，单位界面之间的粘结力。用耐火砖砌筑各种窑炉时，通常在砖与砖之间需用耐火泥浆粘结;某些不定形耐火材并(如投射料、喷涂料、喷补料等)在使用、施工时，要有一定的粘结能力，以使其有效地粘结于施工基体。为了考察粘结剂的性能，确定加入粘结剂的种类和数量，需要测定粘结强度. 中国测定耐火泥浆常温粘结强度的试验方法，分为抗折粘结强度(GB5o24·3)和抗剪粘结强度(GB5o24·4).抗折粘结强度试验方法的要点是用泥浆粘结成试样(图1)，在抗折强度测定仪上进行抗折试验。(图2)介 图2测定抗折粘结强度方法示意图按下式计算抗折粘结强度: R=些 ZbhZ式中R为抗折粘结强度，MPa;F为试样粘结面断裂时的最大载荷，N;L为两支撑辊间的中心距，mm;b为粘结面处试样的宽度，mm;h为粘结面处试样的高度，mm。 抗剪粘结强度的试验方法，是在两块试样之间用耐火泥浆粘结(图3)，干燥后进行剪切试验。 { 阵界‘ 图3测定杭剪粘结强度用试样示意图结果的计算如下: _F 万.~一;州 ~.A式中刀。为抗剪粘结强度;F为试样粘结面断裂时最大载荷;A为试样的粘结面积。 此外，在科研工作中还设计过一些其他方法，如拉伸法(图4)、剪切法(图5)。一自缪一羚 图4拉伸法测定粘结强度示意图一介结界面异 图5剪切法测定粘结强度示意图 不论采取何种方法，应选用自身强度大于被测泥浆粘结强度的试块，否则会出现试块断裂而粘结界面没有断开的现象。 (王通荣)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。