1) high water reducing rate
高减水率
1.
A new type of high-effective retarder and water-reducer with low air entraining content and high water reducing rate for preparing high-strength concretefilled steel pipe is developed by using of polycarboxylate water-reducer and sodium gluconate as well as zinc sulphate.
将聚羧酸减水剂、葡萄糖酸钠、硫酸锌等按一定比例复合,研制出一种高减水率、低引气量的钢管混凝土专用缓凝保塑高效减水剂WUT-G(Ⅰ):配制C 50钢管混凝土时,其最佳掺量为0。
2) water reducing ratio
减水率
1.
And water reducing ratio of concrete is 25%,slump lose a little.
结果表明,X-Z系列减水剂具有缓凝特性,能够显著延缓水泥水化的放热;可使水泥气孔细化且分布更加合理,水泥石的后期水化更充分,水化产物结构更紧密更有力量;减水率达25%,坍落度损失低,各龄期混凝土抗压强度都有较大提高。
2.
By this type of superplasticizer,the water reducing ratio can come up to around 28% and the 28 d strength of the concrete can be increased by 53%.
这类高效减水剂的减水率可达到28%左右,混凝土28 d强度增加53%。
3.
By this type of compounded superplasticizer,the naphthaline dosage can be reduced,higher water reducing ratio(24%~28%) and better slump constant can be achieved for the synergistic effects,and the strength of the concrete can be notably increased by 40%~50%.
复合型高效减水剂降低了萘系减水剂用量,并且产生超叠加效应使复合减水剂具有较高的减水率(24%～28%)和良好的坍落度保持性,可显著提高混凝土的强度40%～50%。
3) water-reducing rate
减水率
1.
Influence of different cement usage to the water-reducing rate in concrete water-reducing admixture;
不同水泥用量对减水剂在混凝土中减水率的影响
2.
The product has good performance,such as low dosage,high water-reducing rate,low slump-loss,and its preparation is simple.
该减水剂与目前市售萘系减水剂相比,具有掺量低、减水率大及混凝土坍落度损失小、抗压强度高等优良性能,且制备工艺简单。
4) water reducing rate
减水率
1.
The sort and application field of water reducing agents are summarized,and water reducing rate,dosage,strength performance of superplasticizer are compared.
综述了减水剂的种类、适用范围,并对常用高效减水剂在减水率、掺量、抗压强度等方面的性能作了比较,指出减水剂研究中所存在的问题,展望了今后的发展趋势,为工程中减水剂的应用起到指导作用。
2.
It has high water reducing rate (over30%),high ability of controlling slump loss(basically no slump los s for2hours)an.
其减水率高(大于30%),保坍性能好(2h坍落度基本无损失),环保性能优良(释放氨的量仅为0。
5) water reduction
减水率
1.
The water reduction and the performance of concrete with the aliphatic superplasticizer modified by sulfanilc acid have extensively enhanced.
在脂肪族类高效减水剂的基础上,添加了对氨基苯磺酸钠,对其进行改性,改性后的减水剂的减水率和混凝土的性能均得到了大幅度提高。
2.
Compared with common melamines superplasticizer, the modified melamine superplasticizer has much higher water reduction and even better strengthening performance.
与亚硫酸氢钠做磺化剂所得减水剂比较,改性后减水剂的减水率及混凝土强度有明显提高。
3.
Tests were carried out on cement paste fluidity, slump loss of products and water reduction of concrete.
根据分子设计的原则,通过改变原料单体摩尔比、酸碱度、反应温度和时间等工艺参数,进行了氨基磺酸系高效减水剂的试验室合成试验,并对产物进行了水泥净浆流动度与其经时变化及混凝土减水率的试验。
6) high water reduction
高减水
补充资料：高吸水高分子材料
高吸水高分子材料
polymeric super-absorbent of water
高吸水高分子材料polymeric super一absorbentof water轻度交联的阴离子型聚电解质，能在较短时间(几秒至几十秒)内，吸持其自身重量300一1000倍，甚至更多的液态去离子水，成为水凝胶的高分子材料。被吸收的水包封在高分子的网络中，即使在加压情况下也不易失去，干燥后可恢复原有的吸水能力。 高吸水高分子材料是美国在20世纪70年代初首先开发出来的。 组成高吸水高分子材料主要由3部分组成:①轻微交联的高分子骨架。多数是亲水性的，具有经基、酞胺基、醚键等亲水结构。有些材料在分子式上看不出有交联点，但实际上是交联的，只是交联机理尚不清楚。交联结构约束吸水，使之只能成为凝胶，而不最终溶解。②连接在高分子链上的阴离子。极大多数是竣基，个别是磺酸基。③与阴离子保持平衡的可移动阳离子。通常是钠离子。密集的阴阳离子，遇水产生渗透压，是吸水动力的主要来源;吸水的另一部分动力，来自高分子结构中的亲水基团和结构，它们通过水化吸附水分。 种类高吸水高分子材料可分两大类:①半合成型。如美国最先开发的就是将丙烯睛接枝共聚在淀粉上，经过皂化，聚丙烯睛链段的氰基一部分水解成梭基，一部分水解成酞胺基，淀粉也可以直接与丙烯酸接枝共聚。纤维素经梭甲基化，再用适当的交联剂交联，也能制造高吸水树脂。②全合成型。简单的如丙烯酸钠在很少量交联剂存在下，甚至不用交联剂而用特种引发剂进行聚合，就可以得到高吸水树脂。将醋酸乙烯酷和丙烯酸甲酷共聚，皂化后得到乙烯醇一丙烯酸钠型高吸水树脂。此外，还有聚氧乙烯型、聚乙烯醉一环状酸醉接枝共聚物型、异丁烯一马来酸共聚物型、醋酸乙烯醋一不饱和二元酸共聚物型等。 用途由于高吸水高分子材料的吸水保水性、吸水后的膨胀性、粘附性、缓释性等，已应用在以下方面。①农业园艺:土壤中加入少量高吸水高分子材料，等于增添了无数微小水库，改善团粒结构，是改良早田土壤的好途径。但因成本高，尚难推广。还在试验探索改造沙漠。用高吸水高分子材料涂覆作物种子(使用量一般为种子的l一2%)，抗旱播种，已在小麦、玉米、棉花、甜菜等作物上取得成功经验。另一实际应用是移栽沾根，在苗木移植上效果更显著。②生理卫生用品:可用高吸水高分子材料代替棉、纸粕生产妇女卫生巾、婴儿纸尿布。它们一般是多层结构、在两层透水纸之间夹一层纸粕和高吸水高分子材料。③土木建筑:高吸水高分子材料与乙烯一醋酸乙烯醋树脂、聚氯乙烯、聚氨酷树脂和橡胶混配，做成各种密封胶、密封件，也用于建筑物嵌缝、地下电缆防水、环管接头密封等方面。高吸水高分子材料遇水膨胀，压迫共混材料堵住一切隙缝，防止渗漏。高吸水高分子材料由于吸水能力受溶解电解质抑止，生产成本比较高，在应用上，尤其农业应用上受到限制。(郑平)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。