1) electrolyte corrosion technique
电解液腐蚀方法
1.
The objective of this paper is to investigate effectiveness and error range of electrolyte corrosion technique applied to acceleration of steel corrosion in concrete.
电解液腐蚀方法常用于诱导混凝土中钢筋的腐蚀以便加快腐蚀速度。
2) electrolytic corrosion
电解腐蚀
1.
Effect of heat treatment on the electrolytic corrosion properties of aluminum based PS plate was studied comparing with high quality 1050 PS plate from abroad by test of polarization curve,SEM,and optical microscope.
结果表明,具有大量细及均匀分布的第二相颗粒和均匀晶粒组织的板基电解腐蚀性能好。
2.
The effect of aluminum lithographic support material on the usage mostly represents on the electrolytic corrosion property.
PS版用铝基材对使用的影响主要表现在电解腐蚀性能方面,影响电解腐蚀的因素很多,从材料角度看其中热处理是主要因素之一。
3.
The thermal shock resistance, flexural strength and static thermal corrosion rates and electrolytic corrosion rates in cryolite molten salt were measured and the cor-rosion process was studied.
采用X射线衍射和扫描电子显微镜对材料的组成和微观结构进行了研究,并测量了样品抗热震性、抗折强度、在冰晶石熔盐中的静态热腐蚀以及电解腐蚀速率,对其腐蚀过程作了初步探讨。
3) electrolysis corrosion
电解腐蚀
1.
The electrolysis corrosion rates in the cryolite molten salt under different current densities were measured and the corrosion mechanism was preliminarily discussed.
用X射线衍射和扫描电子显微镜对材料的组成和微观结构进行了研究,测量了样品在冰晶石熔盐中不同电流密度下的电解腐蚀速率,并对其腐蚀机理作了初步探讨。
4) electrochemical etch
电解腐蚀
1.
Then the alloy coatings were electrochemical etched with specific parameters,resulting in pure copper coatings with nanoporous microstructure.
对合金涂层进行了特定参数的电解腐蚀后,得到了纳米多孔结构的Cu涂层。
5) etching methods
腐蚀方法
1.
Several etching methods of die casting Mg alloy AZ91HP were studied to reveal grain boundries through experiments, including etching after solution heat treatment, direct etching with ammonium chloride saturated solution and electrolytic polishing method.
通过试验研究了压铸镁合金AZ91HP的几种晶粒边界腐蚀方法,包括固溶处理后腐蚀、氯化铵饱和溶液腐蚀和电解抛光腐蚀,并对各种腐蚀方法的结果进行了分析、比较。
6) bingham's etching solution
宾厄姆电解腐蚀液