1) T-weld connector
角型焊接接头
2) fillet joint
角焊接头
3) fillet welding joint
角焊缝接头
4) plain cornerjoint
平头角焊接
5) both side welding (of fillet joint)
(角接头)双面焊接
6) T-welded joint
T型焊接接头
1.
Based on the tearing and cracking at some welding points in al-alloy structure during driving,the low,equal and high strength match for T-welded joints with material AL6063 were simulated,and the influence of stress strain and welding line strength under the condition of static loading on the distributions of stress and strain was also studied in this paper.
针对车辆行驶时铝合金车身上某些焊接部位常常发生开裂的现象,对车身常用的Al6063材料T型焊接接头低、等和高强度匹配进行仿真分析,研究了T型焊接接头受静载荷时的应力应变和焊缝强度对焊接接头应力应变分布的影响。
补充资料：焊接接头晶间腐蚀
焊接接头晶间腐蚀
welded joint intercryctalline corrosion
honjle」}etou jingj旧n fush{焊接接头晶间腐蚀(welded joint intererys-talline eorrosion)在焊接接头处出现的沿晶粒边界发生的腐蚀现象。外观仍可有金属光泽，但实际上晶粒已失去联系，钢质已变脆。在奥氏体不锈钢部位有焊缝晶间腐蚀、敏化区腐蚀和刀状腐蚀等三种不同部位的晶间腐蚀。关于奥氏体不锈钢的晶间腐蚀机理有多种学说，其中以碳化物(如er23e。或(er、Fe)23e。等)在晶界沉淀现象的“贫铬理论”比较为人们所接受。所以为防止这类晶间腐蚀尽量降低含碳量，使焊缝金属含有一定量的稳定元素(如钦、妮等)以防止或降低晶界Cr23C。的形成。此外，焊缝的组织状态也有影响，单相奥氏体组织的焊缝有利于柱状晶的发达，出现贫铬层后会使腐蚀贯穿于晶粒之间，若焊缝为奥氏体了加高温铁素体占的双相组织，由于树枝状被打破，不能构成集中的腐蚀通道。高铬铁素体也会有晶间腐蚀，但与奥氏体钢不同的是从高温急冷下来即有晶间腐蚀倾向，可通过650一85oC加热、缓冷使铬扩散均匀化来消除贫铬层，防止晶间腐蚀。 (许祖泽)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。