3) aerobic granular sludge system
好氧颗粒化
4) oxide powders
氧化物颗粒
1.
Effect of super-fine oxide powders on mechanical properties and microstructures of Sn-58Bi;
超细氧化物颗粒对Sn-58Bi钎料组织及性能影响
5) alumina particle
氧化铝颗粒
1.
That alumina particle was modified with silane coupling agent was discussed,and a condition that the alumina dispersion had thixotropic property was found in to increase surface quality and wet intensity of coating layer,improve the capacity of absorb ink,and decrease the cost of coating layer.
本文用硅烷偶联剂对氧化铝颗粒进行了改性研究,找到了使氧化铝分散液产生触变特性的条件,不但提高了产品的表观质量和涂层的湿膜强度,增大了涂层的吸墨量,还大幅度降低了成本。
2.
The heatresistant steel (HRS) matrix composites reinforced by alumina particles coated with Ni and TiN respectively by means of chemical vapor deposition method are fabricated.
通过化学气相沉积方法在氧化铝颗粒表面分别获得了Ni、TiN涂层。
3.
Chemical vapor deposition is used for coating the surface of alumina particle, and alumina particle/heat resistant steel composites are manufactured by the vacuum infiltration technique.
采用化学气相沉积技术对氧化铝颗粒表面进行涂层处理,通过负压铸渗工艺制备了氧化铝颗粒耐热钢基复合材料,并对其在900℃下的高温磨料磨损特性进行了研究,结果表明:耐热钢在高温下的磨损主要是由磨料的滚压形成的挤出唇、翻边脱落所引起,磨损量较大,而复合材料高温磨损时颗粒突出于基体,承受载荷多,阻碍了磨粒对基体的损伤,因而抗磨性较好,其高温耐磨性是基体材料的33倍多。
6) cao paticles
氧化钙颗粒
补充资料：氧化锆-氧化钇红外陶瓷
分子式： ZrO2-Y2O3
CAS号：
性质：一种以二氧化锆为基体固溶6％～8％(mol)氧化钇的红外光学材料。立方晶结构。熔点2700℃。密度5.98g/cm3。红外透射波段1～10μm。采用1450℃以上高温烧结或1300～1700℃，50～300MPa热压制取。用于制造耐高温红外窗口和整流罩。
CAS号：
性质：一种以二氧化锆为基体固溶6％～8％(mol)氧化钇的红外光学材料。立方晶结构。熔点2700℃。密度5.98g/cm3。红外透射波段1～10μm。采用1450℃以上高温烧结或1300～1700℃，50～300MPa热压制取。用于制造耐高温红外窗口和整流罩。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条