1) sodium ion conductor
钠离子导体
2) sodium fast ion conductor
钠快离子导体
1.
The study of mineral sodium fast ion conductor Na_(1.2+y)Al_(0.1)Yb_yZr_(1.9-y)Si_(0.1)P_(2.9)O_(12) system;
矿物钠快离子导体Na_(1.2+y)Al_(0.1)Yb_yZr_(1.9-y)Si_(0.1)P_(2.9)O_(12)系统的研究
3) Na+ superionic conductor
钠超离子导体
4) ion conductor
离子导体
1.
Fast ion conductors(sometimes are named solid electrolyte) are a kind of solid material which ion conductivity can near or exceed liquid electrolyte.
快离子导体(有时又称固体电解质)是指离子电导率接近有时甚至超过盐溶液和电解质溶液的一类固态材料。
5) Ionic Conductivity
离子导体
1.
Comparison of the Synthesis Methods of Na_5YSi_4O_(12) and Its Ionic Conductivity;
应用交流阻抗谱技术,测定了对用不同方法合成的钠快离子导体Na5YSi4O12纯相的离子电导和离子活化能。
6) Ionic conductor
离子导体
1.
The electrolyte materials, ionic conductor materials, are the key effecting on the efficiency and thermodynamics stability of SOFCs.
其中电解质—离子导体材料是影响固体燃料电池的效率和热力学稳定性的关键 。
2.
The results show that the TaO x films are ionic conductor under the conditions of 150W of depositing power and oxygen contents between 10% and 80%.
结果表明，当溅射功率为１５０Ｗ、氧含量１０～８０％条件下制备的ＴａＯｘ薄膜均为离子导体。
补充资料：钠离子导体
分子式：
CAS号：
性质：是具有钠离子迁移特性的化合物，其典型代表为钠β-氧化铝和Nasicon。此外，尚有Na5MSi4O12和缺陷烧绿石型化合物等。前者代表性化合物有NaGdSi4O12和Na5YSi4O12，在300℃时的电导率分别为3×10-1和1.5×10-1S·cm-1，活化能分别为0.25和0.15eV。后者的通式为A2B2X6X′，其中B2X6形成共顶角的八面值本骨架，在A2X′亚晶格中存在阳离子空位。如NaTa2O5F·Na2O。
CAS号：
性质：是具有钠离子迁移特性的化合物，其典型代表为钠β-氧化铝和Nasicon。此外，尚有Na5MSi4O12和缺陷烧绿石型化合物等。前者代表性化合物有NaGdSi4O12和Na5YSi4O12，在300℃时的电导率分别为3×10-1和1.5×10-1S·cm-1，活化能分别为0.25和0.15eV。后者的通式为A2B2X6X′，其中B2X6形成共顶角的八面值本骨架，在A2X′亚晶格中存在阳离子空位。如NaTa2O5F·Na2O。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条