1) powder of SiO2-P2O5-TiO2
SiO2-P2O5-TiO2粉体
2) SiO2-P2O5-TiO2 electrolyte membrane
SiO2-P2O5-TiO2电解质薄膜
1.
The sol-gel method was applied to prepare the SiO2-P2O5-TiO2 electrolyte membranes with high proton conductivity and chemical stability and low expenditure.
溶胶-凝胶法制备的SiO2-P2O5-TiO2电解质薄膜,具有较高的质子电导率和化学稳定性。
3) CaO-Al2O3-P2O5-SiO2 system
CaO-Al2O3-P2O5-SiO2体系
1.
The water-resistance mechanism of CaO-Al2O3-P2O5-SiO2 system with or without of additional SO4 ions was analyzed by means of XRD and the pore structure analysis.
研究了硫酸根离子对CaO-Al2O3-P2O5-SiO2体系耐水性的影响,通过XRD、SEM及孔结构分析手段对其耐水性机理进行分析。
4) phosphosilicate glass
P2O5-SiO2玻璃
5) phosphosilicate material
P2O5-SiO2材料
1.
Proton-conducting phosphosilicate materials were fabricated by Sol-Gel technique.
结果表明,材料具有微孔结构,含有水分子和形成氢键的质子;在30~70℃,P2O5-SiO2材料电导随温度的升高、磷含量的增加而提高,电导率可达10-2S。
6) SiO2 particles
SiO2粉体
1.
The SEM and XRD analysis results show that the nickel particles on the surface of SiO2 particles were homogeneously crystallized and the cladding was complete gradually with the increase of nickel plating.
为制备质量轻、吸收频段宽的电磁波吸收涂层,采用高压液相氢还原工艺对SiO2粉体进行表面镀镍改性处理,并制备了表面改性SiO2涂层。
补充资料：CaO-TiO2-SiO2 ceramics
分子式：
CAS号：
性质：在CaO-TiO2-SiO2三元系统中以CaSiO3与TiO2或以CaTiSiO5与CaTiO3为基料的陶瓷材料。其结构特点是两种晶相共存，性能受晶相比例影响。配比可在一定范围内调节。主要原料为碳酸钙、二氧化钛、二氧化硅，加入少量改性添加剂，经配料、磨细、混合、成型、烧成等工序获得制品，也可先用碳酸钙和二氧化硅高温下合成硅酸钙，用碳酸钙、二氧化硅、二氧化钛高温下合成钛硅酸钙后再进行配料、烧成等，以确保两晶相共存。主要介电性能为：介电常数80～110，介质损耗角正切值(0.8～2.5)×10-4，介电常数温度系数(-450～+550)×10-6/℃。抗电温度(45～55)kV/mm，电阻率(1011～1012)Ω·cm。主要用作温度补偿型陶瓷电容器瓷料。
CAS号：
性质：在CaO-TiO2-SiO2三元系统中以CaSiO3与TiO2或以CaTiSiO5与CaTiO3为基料的陶瓷材料。其结构特点是两种晶相共存，性能受晶相比例影响。配比可在一定范围内调节。主要原料为碳酸钙、二氧化钛、二氧化硅，加入少量改性添加剂，经配料、磨细、混合、成型、烧成等工序获得制品，也可先用碳酸钙和二氧化硅高温下合成硅酸钙，用碳酸钙、二氧化硅、二氧化钛高温下合成钛硅酸钙后再进行配料、烧成等，以确保两晶相共存。主要介电性能为：介电常数80～110，介质损耗角正切值(0.8～2.5)×10-4，介电常数温度系数(-450～+550)×10-6/℃。抗电温度(45～55)kV/mm，电阻率(1011～1012)Ω·cm。主要用作温度补偿型陶瓷电容器瓷料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。