1) decrepitated spodumene
焙烧锂辉石
1.
Effectiveness of decrepitated spodumene in inhibiting alkali-silica reaction;
焙烧锂辉石对碱硅酸反应的抑制效果
2) β-spodumene
β-锂辉石
1.
It is found out that the main phase was always β-spodumene in spite of increase of the heating temperature from 820℃.
运用X射线衍射分析、扫描电子显微镜以及激光拉曼散射,结合LAS微晶玻璃的热膨胀性能和力学性能,对不同热处理制度的试样进行结构和性能研究,结果表明:随着晶化温度的升高,微晶玻璃的主晶相未发生改变,都为β-锂辉石,但晶体含量不断升高,晶粒尺寸逐渐变大。
2.
When heating the dried gels from 700℃ to 1200℃ for 2h,hexagonal β-quartz solid-solution first crystallized and then gradually transformed into tetragonal β-spodumene solid-solution with increasing temperature.
研究表明:热处理温度在700～1200℃时,LASZ微粉先形成六方晶系的β-石英固溶体,随热处理温度的升高,逐渐转变为稳定的四方晶系β-锂辉石固溶体。
3.
Lithium aluminosilicate glass-ceramics with β-spodumene composition were prepared by the sol–gel process from three different aluminum sources, namely, aluminum nitrate, aluminum nitrate and aluminum isopropoxide with a molar ratio of 1:1 and aluminum isopropoxide.
而完全采用异丙醇铝或部分采用异丙醇铝为铝源的样品中,最终得到的是β-锂辉石相。
3) spodumene
[英]['spɔdju,mi:n] [美]['spɑdʒə,min]
锂辉石
1.
Formation and Characterization of Whisker-like β-spodumene in LAS Glass-ceramics;
锂铝硅微晶玻璃中纤维状β-锂辉石晶相的形成和表征
2.
Flotation of spodumene and beryl with a new collector;
新型捕收剂浮选锂辉石和绿柱石
3.
Experiment on the Flotaion of Spodumene Using New-type Collectors;
新型捕收剂浮选锂辉石矿的试验研究
5) aglaite
变锂辉石
6) calciend Li mica
焙烧锂云母
补充资料：锂辉石陶瓷
分子式：
CAS号：
性质：锂辉石(Li2O·Al2O3·4SiO2)为主晶相的陶瓷。相对介电常数8.5～9，介电常数温度系数具有较大的正值，介质损耗角正切值(150～200)×10-4。具有较低的线膨胀系数，热稳定性良好，经1000℃至冷水的淬冷试验不产生裂纹。主要原料为碳酸锂、氧化铝、二氧化硅和黏土，经高温烧结而成。但烧成温度范围狭窄。可用于制造燃气轮机的叶片、喷气发动机的喷嘴等。还可制作日用耐热高级砂锅等。
CAS号：
性质：锂辉石(Li2O·Al2O3·4SiO2)为主晶相的陶瓷。相对介电常数8.5～9，介电常数温度系数具有较大的正值，介质损耗角正切值(150～200)×10-4。具有较低的线膨胀系数，热稳定性良好，经1000℃至冷水的淬冷试验不产生裂纹。主要原料为碳酸锂、氧化铝、二氧化硅和黏土，经高温烧结而成。但烧成温度范围狭窄。可用于制造燃气轮机的叶片、喷气发动机的喷嘴等。还可制作日用耐热高级砂锅等。