1) steel fiber reinforced polymer cement mortar
钢纤维增强聚合物水泥砂浆
1.
A feasibility argumentation of using steel fiber reinforced polymer cement mortar as a rigid waterproofing roof;
钢纤维增强聚合物水泥砂浆刚性屋面防水层的可行性论证
2.
In order to solve the roof leakage problems now widely existed in buildings at home and abroad, this paper proposed the using of steel fiber reinforced polymer cement mortar /concrete (SFPCC) as a rigid waterproofing roof material to substitute at the conventional flexible one.
针对目前国内外普遍存在的屋面防水问题 ,依据聚合物与水泥复合有利于改善材料内部结构密实度以及聚合物和钢纤维能改善材料变形能力的特性 ,提出用钢纤维增强聚合物水泥砂浆作为刚性屋面防水材料的设想 ,通过对钢纤维聚合物水泥砂浆的韧性试验 ,论证了此种材料在技术上是可行
4) steel fiber reinforced cement(SFCEM)
钢维增强水泥砂浆
5) steel fiber-reinforced mortar
钢纤维增强砂浆
1.
Direct tensile damage mechanic model of steel fiber-reinforced mortar;
钢纤维增强砂浆的轴拉损伤力学模型
6) steel fiber reinforced mortar
钢纤维水泥砂浆
1.
In the present study, the tensile stress-crack opening relationship of steel fiber reinforced mortar (SFRM) is determined by inverse analysis using load versus crack mouth opening displacement (CMOD) curve from notched beam tests.
该文根据三点弯曲缺口梁的荷载与裂缝张开位移(CMOD)曲线用反分析法确定了钢纤维水泥砂浆的σ-w关系。
2.
The residual tensile strength of steel fiber reinforced mortar(SFRM) was determined by inverse analysis by using load versus crack mouth opening displacement(CMOD) curve from notched beam tests.
根据三点弯曲缺口梁的荷载与裂缝张开位移曲线,用反分析法确定了钢纤维水泥砂浆的拉伸残余强度。
补充资料：玻璃纤维增强液晶聚合物
分子式：
CAS号：
性质：由玻璃纤维和液晶聚合物通过螺杆挤出机熔融共混挤出形成的材料。由于液晶聚合物在微小的外力作用下极容易取向，使成品力学性能呈显著的各向异性，制品接缝强度低，应用领域受到极大的限制。经玻璃纤维增强后，不仅克服上述缺点，降低了成本，而且拉伸强度由116MPa提高到137.3MPa，拉伸模量由9.6GPa提高到15.9GPa，使用温度也有所提高。已成为液晶聚合物的主流商品，在航空、电子、电器等领域中具有广泛的用途。
CAS号：
性质：由玻璃纤维和液晶聚合物通过螺杆挤出机熔融共混挤出形成的材料。由于液晶聚合物在微小的外力作用下极容易取向，使成品力学性能呈显著的各向异性，制品接缝强度低，应用领域受到极大的限制。经玻璃纤维增强后，不仅克服上述缺点，降低了成本，而且拉伸强度由116MPa提高到137.3MPa，拉伸模量由9.6GPa提高到15.9GPa，使用温度也有所提高。已成为液晶聚合物的主流商品，在航空、电子、电器等领域中具有广泛的用途。