1) unstable fracture toughness
失稳断裂韧度
1.
According to the measured maximum load P_(max) and the corresponding crack mouth opening displacement CMOD_c the unstable fracture toughness K~(un)_(Ic) of cement paste and mortar were evaluated.
根据水工混凝土断裂试验规程,利用试验中测得的最大荷载及对应的裂缝口张开位移计算了水泥净浆和水泥砂浆的失稳断裂韧度,并通过电阻应变片法确定的起裂荷载得到了二者起裂韧度的实测值。
2) stable fracture tenacity
稳定断裂韧度
1.
Besides,fatigue equation is used to establish the relationship between load repetition and stable fracture tenacity descent,which exp.
同时,利用疲劳方程建立了荷载作用次数与稳定断裂韧度下降之间的关系式,由此说明疲劳荷载作用下产生的累计损伤导致的稳定断裂韧度下降是路面开裂破坏的根本原因。
3) unstable fracture toughness
失稳韧度
1.
Influence of shape of specimens on unstable fracture toughness K_(IC)~(un) of concrete;
试件形式对混凝土失稳韧度K_(IC)~(un)的影响
2.
At present,two kinds of geometry shape specimens,three-point bending beam and wedge splitting specimen are often used to test the unstable fracture toughness Kun IC of concrete.
为了确定用三点弯曲梁和楔入劈拉两种形式试件所测的混凝土失稳韧度是否相同以及有多大差异,从两种形式试件的比值入手,对二者失稳韧度的关系进行了分析。
4) fracture toughness
断裂韧度
1.
CTOD fracture toughness of welded joint of TCS stainless steel;
TCS不锈钢焊接接头CTOD断裂韧度试验研究
2.
Microstructure and fracture toughness of joint under different welding conditions;
不同焊接条件下接头组织和断裂韧度的对比分析
3.
Numerical simulation and study on fracture toughness of submarine pipeline;
海底管线用钢低温断裂韧度的试验研究和数值模拟
补充资料：裂纹失稳扩展
分子式：
CAS号：
性质：材料内部裂纹尖端的应力场强度因子达到或超过材料的断裂韧性之后发生的裂纹快速扩展。裂纹失稳扩展将导致材料迅速断裂。
CAS号：
性质：材料内部裂纹尖端的应力场强度因子达到或超过材料的断裂韧性之后发生的裂纹快速扩展。裂纹失稳扩展将导致材料迅速断裂。