1) volume parameter
体积参数
1.
Through Marshall test of AC-13 asphalt mixture under various molding temperatures the volume parameters of Marshall members are analyzed.
通过对AC-13沥青混合料在不同的成型温度下进行马歇尔试验,分析马歇尔试件的各种体积参数,模拟不同碾压温度对体积参数的影响,探求规律,指导沥青路面的现场施工。
2.
Dynamic modulus(E*) tests are performed on various void volume samples under the conditions of various temperatures and various loading frequencies,which are obtained from asphalt mixtures with Superpave gradation,and the changing regularity of dynamic modulus of asphalt mixtures with the volume parameters and loading condition is analyzed.
对一种Superpave级配沥青混合料不同空隙率的试样进行了不同温度、不同加载频率条件下动态模量试验,分析了混合料动态模量随体积参数、加载条件的变化规律,研究结果对我国的路面设计模量动态参数的选择具有借鉴意义。
3.
The VA,VMA and VFA and the other volume parameter has the important influence with the performance of asphalt mixture s mechanics performance,construction performance and pavement performance.
压实空隙率、矿料间隙率和沥青饱和度等体积参数对沥青混合料的力学性能、施工性能和路用性能有重要影响,三者之间也存在着相互制约关系。
2) volumetric parameter
体积参数
1.
Relationship between volumetric parameters of bituminous mixture and its high-temperature performance;
沥青混合料体积参数与高温性能间的关系
2.
Combined with Chinese actual situation of engineering, from the aspects of the raw material choice, gradations decision, the method of moulded specimen, the mixture volumetric parameters, performance evaluation etc, a set of volumetric design method of target mixing ratio for asphalt mixture based on Marshall test was put forward by using the experience of American Superpave for reference.
借鉴美国Superpave沥青混合料设计方法,结合中国的生产实际,从原材料的选择、级配的确定、成型试件的方法、混合料体积参数指标、计算方法以及性能评价等方面,提出一套完整的以马歇尔试验为基础的沥青混合料体积设计方法。
3.
Using statistical regression tools,the influence of aggregate gradation and asphalt content on volumetric parameters and densification properties of HMA are studied.
从体积设计的角度 ,分析沥青混合料的旋转压实 (SGC)曲线 ,研究在压实过程中沥青混合料体积参数的变化特征。
3) Volume parameters
体积参数
1.
Research on the volume parameters of SMA mixture;
SMA混合料体积参数的研究
2.
Using the volume design method,effects of volume parameters on workability of road concrete were researched by experiment research.
采用体积设计法,试验研究了粗细集料体积比(Vcf)、细集料与水泥浆体体积比(Vfp)等体积参数对道路混凝土工作性能的影响。
4) global parameterization method
体积参数法
5) dose-volume parameters
剂量-体积参数
6) universal volumetric chart
体积参数通用图
补充资料：保留体积
分子式：
CAS号：
性质：保留时间内流经色谱柱的流动相体积，即待测组分从进样到出现峰最大值所需的流动相的体积。
CAS号：
性质：保留时间内流经色谱柱的流动相体积，即待测组分从进样到出现峰最大值所需的流动相的体积。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条