2) crack growth life
裂纹扩展寿命
1.
Based on the research of mechanical performance, crack growth rates and crack growth life for 30CrMnSiNi2A and GC4 steel were analyzed statistically on the same crack length condition.
在分析30CrMnSiNi2A和GC4力学性能的基础上,在相同裂纹长度条件下,对两种材料的裂纹扩展寿命和裂纹扩展速率的统计特性进行了统计研究。
2.
The tests of crack initiation life under the fighter spectra and crack growth life under the freighter spectra are conducted.
介绍了在战斗机谱载作用下的３０ＣｒＭｎＳｉＮｉ２Ａ和ＬＹ１２ＣＺ试件的裂纹形成寿命试验，以及在运输机谱载作用下的３０ＣｒＭｎＳｉＡ和ＬＹ１２ＣＺ试件的裂纹扩展寿命试验。
3.
The assessment of the increase of crack growth life after hole cold expanding is addressed.
本文用含孔边穿透裂纹的冷胀孔、未胀孔剩余寿命之比来评价孔冷胀强化工艺延长裂纹扩展寿命的效果。
3) Crack Propagation Life
裂纹扩展寿命
1.
Reliability and sensitivity analysis of a Turbine Disk crack propagation life
涡轮盘裂纹扩展寿命可靠性灵敏度分析
2.
Reliability analysis of turbine disk crack propagation life with arbitrary distribution parameters
任意分布参数的涡轮盘裂纹扩展寿命可靠性分析
3.
As an examole of analysing the fatigue crack of wing spar in type 5 Fighter-Trainer, The methods of crack propagation life prediction by means of fractography and Zheng-Hirt formula are ntrodued in this paper.
以歼教五机翼主梁疲劳断裂分析为例 ,介绍了用断口金相和Zheng -Hirt公式估算疲劳裂纹扩展寿命的方法 ,为研究老龄飞机的使用寿命问题 ,进行了有益的探
4) crack life prediction
裂纹寿命预测
5) Fatigue crack propagation life
疲劳裂纹扩展寿命
1.
The fatigue crack initiation life and the fatigue crack propagation life are quite different in each failure style.
在五种不同的破坏情况下,疲劳裂纹初始寿命和疲劳裂纹扩展寿命均不同,必须分阶段评估,这也直接影响到整体疲劳寿命的预计;此时常规的、经典的疲劳裂纹扩展理论难以直接应用。
6) fatigue life-crack propagation
疲劳寿命-裂纹扩展
补充资料：裂纹失稳扩展
分子式：
CAS号：
性质：材料内部裂纹尖端的应力场强度因子达到或超过材料的断裂韧性之后发生的裂纹快速扩展。裂纹失稳扩展将导致材料迅速断裂。
CAS号：
性质：材料内部裂纹尖端的应力场强度因子达到或超过材料的断裂韧性之后发生的裂纹快速扩展。裂纹失稳扩展将导致材料迅速断裂。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。