1) Zn1-xCoxO thin films
Zn1-xCoxO薄膜
1.
Zn1-xCoxO thin films,when the exterior magnetic fields are paraell or vertical for the face of films,the room temperature coercive force are only 6～7 G,show the characters of diulted magnetic semoconductor(DMS)and isotropy.
对Zn1-xCoxO薄膜的磁特性测量结果表明:薄膜具有室温(300 K)铁磁性;Zn1-xCoxO薄膜,无论外部磁场平行或垂直于薄膜平面,其室温矫顽力均仅为6~7 G,呈现典型的稀磁及磁各向同性特征;而对于多晶Zn1-xCoxO薄膜,其室温矫顽力在200~370 G之间展示出显著的磁化各向异性特征;同时讨论了薄膜的铁磁性起源及其各向异性机理。
2) Zn1-xCoxO crystal
Zn1-xCoxO晶体
1.
Zn1-xCoxO crystals were synthesized by chemical vapor transport method at 970℃ on the sapphire substrate and quartz substrate,respectively in this paper.
本文采用高温化学气相输运法,温度970℃,在蓝宝石和石英基片上制备Zn1-xCoxO晶体。
3) Zn1-x MnxO thin films
Zn1-xMnxO薄膜
4) Zn 1-xCd xO films
Zn1-xCdxO薄膜
5) Zn1-xMgxO films
Zn1-xMgxO薄膜
1.
The effects of Mg content on structural and transmittance properties of Zn1-xMgxO films were studied.
采用超声喷雾热解法,在Si(100)和石英玻璃衬底上,生长出没有相偏析、结晶质量好、不同组分比的Zn1-xMgxO薄膜(x=0。
6) Zn1-xMgxS thin film
Zn1-xMgxS薄膜
1.
The solid-solution semiconductor Zn1-xMgxS thin films were grown by vacuum co-evaporation of ZnS and Mg powders on quartz glass substrate.
以ZnS、Mg粉末为原料,应用双源真空蒸镀法,在石英玻璃衬底上成功地制备了不同Mg含量x的三元固溶体半导体Zn1-xMgxS薄膜。
补充资料：ACTH-Zn
分子式：
CAS号：
性质：又称氢氧化锌促皮质素，长效促皮质素。由精制促皮质素吸附氢氧化锌而得的悬浮液，pH值7～8。于2～10℃贮存可保持活性两年以上。因含有结合的氢氧化锌，能抑制体内蛋白酶对促皮质素的水解，显著减慢人体内对促皮质素的吸收速度，而具有延效作用。见促皮质素。
CAS号：
性质：又称氢氧化锌促皮质素，长效促皮质素。由精制促皮质素吸附氢氧化锌而得的悬浮液，pH值7～8。于2～10℃贮存可保持活性两年以上。因含有结合的氢氧化锌，能抑制体内蛋白酶对促皮质素的水解，显著减慢人体内对促皮质素的吸收速度，而具有延效作用。见促皮质素。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条