1) PZT-95/5 ferroelectric ceramic
PZT-95/5铁电陶瓷
1.
With a light gas gun for generating the shock wave loading,the PZT-95/5 ferroelectric ceramic has been shock compressed to induce a phase transformation for electric depoling.
利用轻气炮作为加载手段,对PZT-95/5铁电陶瓷进行冲击波压缩,以实现陶瓷受激相变放电。
2) PZT-95/5 ceramic
PZT-95/5陶瓷
1.
In this paper, basing on a principle that two-wave can be detected when structure phase transition occurs, we measured the phase transformation pressure from the ferroelectric phase to the antiferroelectric phase of national PZT-95/5 ceramic under shock loading .
本文对国产的PZT-95/5陶瓷在冲击波作用下发生铁电相(FE)→反铁电相(AFE)的相变压力进行了实验研究。
3) PZT-5 ferroelectric ceramics
PZT-5铁电陶瓷
4) PZT ceramics
PZT铁电陶瓷
5) PZT-5H ferroelectric ceramics
PZT-5H铁电陶瓷
补充资料：反铁电陶瓷
分子式：
CAS号：
性质：主晶相为反铁电体的陶瓷材料，常见的反铁电体为锆酸铅(PbZrO3)或以其为基的固溶体。具有高的相变场强、储能密度和较低的介电常数，低的介质损耗。如Pb0.97La0.02[(Zr59Till)0.7Sn0.3]O3反铁电陶瓷相变场强为34kV/cm(25℃)，介电常数峰值2020，居里温度181℃。采用一般电子陶瓷工艺制造。由于其中含铅量较高，常用刚玉坩埚加盖密封烧成，以防止氧化铅高温挥发，烧成温度：1340℃左右。用这类材料制成的抗辐射储能电容器的储能密度可达0.3J/cm3以上，制作时常在瓷片电极附近的绝缘边上涂敷半导釉，可有效地防止绝缘边击穿，提高工作电压。还可用于制作高压电容器、高介电容器，以及换能器(实现电能与机械能转换)等。
CAS号：
性质：主晶相为反铁电体的陶瓷材料，常见的反铁电体为锆酸铅(PbZrO3)或以其为基的固溶体。具有高的相变场强、储能密度和较低的介电常数，低的介质损耗。如Pb0.97La0.02[(Zr59Till)0.7Sn0.3]O3反铁电陶瓷相变场强为34kV/cm(25℃)，介电常数峰值2020，居里温度181℃。采用一般电子陶瓷工艺制造。由于其中含铅量较高，常用刚玉坩埚加盖密封烧成，以防止氧化铅高温挥发，烧成温度：1340℃左右。用这类材料制成的抗辐射储能电容器的储能密度可达0.3J/cm3以上，制作时常在瓷片电极附近的绝缘边上涂敷半导釉，可有效地防止绝缘边击穿，提高工作电压。还可用于制作高压电容器、高介电容器，以及换能器(实现电能与机械能转换)等。