1) edgewise crush resistance
边压强度
1.
The puncture strength,edgewise crush resistance and adhesive strength of double-wall corrugated paperboard with A&B flutes were studied by a series of tests under four different ambient conditions of temperature 20℃ and relative humidity of 60%,70%,80% and 90%,and the change rule of mechanical properties of double-wall corrugated paperboard with relative humidity were obtained.
测试分析了AB型双瓦楞纸板在环境温度20℃和4种相对湿度(60%、70%、80%、90%)组合条件下的戳穿强度、边压强度、粘合强度,获得了这些力学性能随相对湿度变化的规律。
2.
In this paper,the interreiation has been researched for edgewise crush resistance and puncture esistance of the corrugated fibreboard.
本文分析研究了瓦楞纸板边压强度与戳穿强度检测指标间的相关性问题，求得了几种高度显著的相关拟合方程和图象。
2) edge crush strength
边压强度
1.
The edge crush test(ECT) and bursting strength test(BST) was performed,and the experimental data was processed by the software of SAS,and a regression equation of edge crush strength and bursting strength of the corrugated board was established.
通过试验,研究了五层瓦楞纸板强度与原纸强度的关系,利用SAS软件对试验结果进行分析,得出五层瓦楞纸板边压强度和耐破度计算的回归方程。
2.
This paper introduced the quality criterion,the test procedure and control methods of corrugated paper carton,including paper quality,paper thicness, adhesive strength,punctured strength,edge crush strength and presswork quality etc.
本文介绍了瓦楞纸质量、瓦楞纸板厚度、啤酒箱黏合强度、戳穿强度、边压强度和面纸印刷等的质量要求、检测方法以及质量控制措施。
3) edge compressive strength
棱边抗压强度
5) edge intensity
边缘强度
1.
At last,the binary images after segmenting the fingerprint images are obtained by the local adaptive thresholds relying on the edge intensity of images.
提出了一种合理有效的指纹图像二值化方法,先利用Kirsch算子得到指纹图像的方向场,然后对指纹图像进行方向中值滤波,最后通过图像的边缘强度设计局部自适应阈值对指纹图像进行分割,从而得到二值化图像。
2.
First,it rtransformed the image space form RGB to YCbCr,and found the maximal edge intensity in a 3×3 neighborhood.
该方法首先将彩色图像从RGB空间转换到YCbCr空间,分别求出三个子空间中像素在3×3邻域内的最大边缘强度值;然后采用Tsallis熵求取每一个子空间的最佳边缘强度阈值对亮度子空间Y和颜色信息子空间Cb、Cr分别进行边缘提取,最后将三个子空间中获取的边缘点进行融合,从而完成整幅图像的边缘检测。
6) edge strength
边缘强度
1.
The edge strength of Intra frames and Inter frames are computed respectively,taking units of 4×4 block.
264中去块效应滤波的理论进行了再分析,提出了一种以4×4块为单位,对帧内预测帧和帧间预测帧分别计算边缘强度(Bs)的快速去块效应滤波算法。
补充资料：等离子体压强和磁压强
在流体近似下，可以把等离子体看成是彼此相互作用的电子和离子两种气体的混合物。它们各具有动力压强,上述两种气体成分的分压强之和P=k(niTi+neTe)称为等离子体压强，k是玻耳兹曼常数,角标i、e分别表示离子和电子。
经常遇到的处在静磁场 B中的等离子体，除了等离子体压强外，它还受到磁力 作用，j是电流密度。当磁力线是直的并互相平行时，(B·墷)B项等于零，相当于压强，称为等离子体磁压强。
在等离子体压强和磁压强并存之时，常用参数表示磁压强的相对重要性。这个参数称为比压。
经常遇到的处在静磁场 B中的等离子体，除了等离子体压强外，它还受到磁力 作用，j是电流密度。当磁力线是直的并互相平行时，(B·墷)B项等于零，相当于压强，称为等离子体磁压强。
在等离子体压强和磁压强并存之时，常用参数表示磁压强的相对重要性。这个参数称为比压。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条