1)  Molybdenum residue of ammonia leaching
氨浸钼渣
2)  Ammonia leaching residue
氨浸渣
1.
The absorption of methyl orange by ammonia leaching residue of manganese nodule is investigated.
研究大洋锰结核氨浸渣对甲基橙染料废水的吸附行为。
2.
A new type of water-disperse anticorrosive paint was prepared by using ammonia leaching residue which is the residues of manganese nodules after the extraction of Co, Ni, Cu by ammonia leaching process.
以大洋锰结核经氨浸工艺提取钴、镍、铜等金属后的粉末状固体残渣(氨浸渣)为颜填料、与水混合制成色浆,再与苯丙乳液和辅助原料混合,制备水性防锈涂料。
3.
The effect of ammonia leaching residue which is the residues of manganese nodules after the extraction of Co,Ni,Cu by ammonia leaching process was studied on the sintering behavior and properties of quartzfeldspar-kaolin ternary system ceramics.
通过研究大洋锰结核经氨浸工艺提取Co,N i,Cu等有价金属后的粉末状固体残渣(氨浸渣)对石英-长石-高岭土3组分陶瓷体系烧结行为及制品性能的影响发现:3组分体系中添加不超过10%的氨浸渣,在1 140℃烧结90 m in,烧结体的抗折强度大于65。
3)  ammonia leaching residues
氨浸渣
1.
Results show that extraction ratio reaches 85% in ammonia leaching residues,and the qulity of ammonium molybdates meet Grade I inner quality standard of our company.
介绍了氨浸渣采用加入合适的添加剂和氨水进行配料→氨压→过滤→洗涤以及滤渣的再次处理等过程回收金属钼并生产钼酸铵的工艺。
2.
The leval of granulated substance,such as ferri calcium silicon,and so on may affect the remained molybdenum of ammonia leaching residues in molybdate production.
当酸盐预处理不彻底时,既造成渣含钼升高,又增加了净化的负担;若酸洗时加酸洗助剂则可强化除杂,使氨浸渣中可溶钼含量及产渣率大大降低,一次回收率可达97%以上,同时酸盐预处理时间缩短,生产效率提高,辅料消耗减少,生产成本降低。
4)  ammonium leaching of molybdenum trioxide
钼的氨浸取
5)  reduction-ammoniacal leaching residue
还原氨浸渣
1.
33) for lithium ion-sieve precursor is synthesized by a solid-state reaction of LiOH and reduction-ammoniacal leaching residue(MnCO_3) of polymetallic nodules.
以LiOH和多金属结核还原氨浸渣为原料,用固相反应法合成了具有正尖晶石结构的锂离子筛前驱体Li1+xMn2-xO4(0
2.
33) made by synthesis of LiOH and reduction-ammoniacal leaching residue of polymetallic nodules is studied based on the analysis of the microstructure and surface features of modified Li-IS with XRD,SEM,TEM,TG-DTA and BET.
通过X射线衍射、差热-热重分析、比表面积、孔体积等方法分析酸洗得到离子筛的微观结构及表面特征,研究以Li-OH和多金属结核还原氨浸渣为原料合成的正尖晶石结构的锂离子筛前驱体Li1+xMn2-xO4(0