1) aluminium copper zinc alloy
铝-铜合金
2) copper-aluminum alloy
铜铝合金
1.
The copper-aluminum alloy was prepared by infiltration with the methods of copper powder compact wrapped by aluminum sheet and embed in aluminum powder.
采用铝片包裹和铝粉包埋铜粉压块的方法,通过熔渗制备铜铝合金,铝片包裹法在真空、空气及氩气气氛下进行实验,铝粉包埋法在氩气气氛下进行实验,温度为750℃,保温6h。
3) Al-Cu alloy
铝铜合金
1.
The study of microstructure and mechanical properties of high strength and toughness casting Al-Cu alloy;
高强铸造铝铜合金显微组织与力学性能的研究
2.
Influence of process parameter of MIG welding on the weld of Al-Cu alloy;
工艺参数对MIG焊铝铜合金焊缝组织的影响
3.
Effects of electromagnetic stirring on the shape,structure and mechanical properties of pulse metal inert gas(MIG) weld of 2219 Al-Cu alloy were investigated.
研究电磁搅拌对2219铝铜合金脉冲MIG焊焊缝形状、组织及性能的影响。
4) aluminum-copper alloy
铝铜合金
1.
Current status of anodic oxidation of aluminum-copper alloy;
铝铜合金阳极氧化发展概况
2.
In low concentration mixed solutions,a silvery white film with excellent appearance and higher hardness and thickness was obtained on aluminum-copper alloy difficult to anodize by using grading voltage and high temperature.
在低浓度复合电解液中,利用分阶段升压技术,高温下在阳极氧化较难的铝铜合金LY 12上制备了具有较高厚度、硬度和良好外观的银白色氧化膜层。
3.
The content of copper residue on the surface of the electrolytic capacitor cathode foil of aluminum-copper alloy is usually more than 50 mg/m2.
利用铝铜合金电子铝箔生产的铝电解电容器用阴极箔的表面附着铜含量一般高达50mg/m2以上。
5) Cu-Al alloy
铜铝合金
1.
Research on correlation between Streptococcus mutans adhesion and surface roughness of Cu-Al alloy and Co-Cr alloy;
变形链球菌黏附对铜铝合金、钴铬合金表面粗糙度影响的初步研究
2.
The complicated procedure and high cost of internal oxidation of aluminum in Cu-Al alloy have severely limited the widespread application of high-quality copper strengthed by nanometer alumina through internal oxidation of aluminum in Cu-Al alloy.
研究了铜铝合金内氧化与外氧化的条件,提出了氧化层厚度的动力学模型。
6) Al-Si-Cu Alloy
铝硅铜合金
1.
According to researching technical speciality of Al-Si-Cu alloy,making choice of fit clearance of die casting mould shaped part is necessary,then in virtue of mould temperature-controller and midway anneal measure gains the results of increasing quality of die casting and prolonging service life of mould.
通过对铝硅铜合金工艺特性的研究，提出选定合理的压铸模成形零件配合间隙的必要性，并借助模具温控装置、模具中间退火等工艺措施，达到既提高压铸件的质量，又延长压铸模使用寿命的目的。
补充资料：锌铝铜合金
分子式：
CAS号：
性质：应用最广的一种锌合金。除了铝和铜外，往往加入少量镁。常用牌号有ZnAl10-5、ZnAl10-1、ZnAl14-1和ZnAl0.2-4。加入铝可以显著提高强度和冲击韧性；铜可以提高锌的硬度、强度和冲击韧性；镁可以提高合金冷轧后的强度。这类合金熔融法制备，既可浇注成铸件，也可以通过塑性加工成材。在工业上常用作黄铜的代用品，用作要求尺寸稳定的各种零件。
CAS号：
性质：应用最广的一种锌合金。除了铝和铜外，往往加入少量镁。常用牌号有ZnAl10-5、ZnAl10-1、ZnAl14-1和ZnAl0.2-4。加入铝可以显著提高强度和冲击韧性；铜可以提高锌的硬度、强度和冲击韧性；镁可以提高合金冷轧后的强度。这类合金熔融法制备，既可浇注成铸件，也可以通过塑性加工成材。在工业上常用作黄铜的代用品，用作要求尺寸稳定的各种零件。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。