1) micro-sized spherical nickel hydroxide
微米级球形氢氧化镍
1.
Performance comparison between nano-sized and micro-sized spherical nickel hydroxide;
纳米级氢氧化镍与微米级球形氢氧化镍性能比较
2) nano-sized nickel hydroxide
纳米级氢氧化镍
1.
Micro-sized spherical and nano-sized nickel hydroxide were synthesized by using co-precipitation and precipitation transform methods respectively to develop Ni-MH battery with high specific capacity and cycle life performance,and their structures,morphology and electrochemical performance were compared by X-ray diffraction,charge discharge and cyclic voltammetry tests.
为开发高容量、高循环性能镍氢电池,分别使用共沉淀法和固相沉淀转化法,合成了微米级球形氢氧化镍和纳米级氢氧化镍,并对其结构、形貌以及电化学性能进行了对比研究。
3) spherical Ni(OH)2
球形氢氧化镍
1.
The spherical Ni(OH)2 particles were synthesized by controlled crystallization method in a continuous stirring tank reactor, their outer and interior structures were characterized by electronic microscope technologies, and the crystallization growth mechanisms and the effects of Ostwald ripening during growth processes were discussed.
利用控制结晶方法在连续搅拌反应器中制备了球形氢氧化镍,通过电子显微技术表征了球形氢氧化镍的内外结构并讨论了其生长过程机理和Ostwald熟化的作用。
4) spherical Ni(OH)_2
球形氢氧化镍
1.
Study on structural characteristics of spherical Ni(OH)_2 electrode active materials;
电极活性物质球形氢氧化镍的结构特征研究(英文)
2.
The spherical Ni(OH)_2 is synthesized with controlled crystallization method in a continuous stirring tank reactor.
利用控制结晶方法在连续搅拌反应器中制备了球形氢氧化镍,通过电子显微技术表征了球形氢氧化镍的内外结构并研究了其生长过程中的陈化现象。
3.
The microstructures of spherical Ni(OH)_2 was studied, and the preparation, the structure, and the relationships between them were carefully and systematically discussed.
对球形氢氧化镍的制备、结构和性能及三者之间的相互关系进行了较全面系统的研究,探讨了其生长过程特征和微结构形成机理,对产品电化学活性的影响因素及其电极过程动力学进行了再认识。
5) Spherical nickel hydroxide
球形氢氧化镍
1.
Preparation of the high-density,high-activity,and spherical nickel hydroxide and its performance controll;
高密度高活性球形氢氧化镍的制备与性能控制
2.
Taking nickel compounds as main raw materials and using new technology of ligand catalytic liquid phases precipitation,spherical nickel hydroxide of nanometer is producted.
以镍盐为主要原料 ,采用配位催化液相沉淀新技术 ,生产的纳米级球形氢氧化镍 ,具有高纯度、高密度、高容量、高活性 ,稳定性、均匀性好的特
3.
The poor high-temperature performance of the spherical nickel hydroxide becomes the main reason for limitation of use as the positive electrode active material in MH-Ni battery, especially for the vehicle power.
球形氢氧化镍的高温性能已经成为制约其应用于动力型MH—Ni电池的主要因素。
6) spherical β-nickel hydroxides
β-球形氢氧化镍
1.
Microstructures of spherical β-nickel hydroxides and their thermal decomposition characteristics;
β-球形氢氧化镍的微结构与热分解特征
补充资料：镍阳极板和氧化镍制备车间设计
镍阳极板和氧化镍制备车间设计
design of plant for preparation of nickel anode and nickel oxide
n ieyang』iban he yanghuanie zhibei ehe』ian sheli镍阳极板和级化裸制备车间设计(designofplant for preparation of niekel anode and niek-el oxide)以高镍镜磨浮分离车间产出的硫化镍精矿为原料，生产供镍电解精炼用镍阳极板或商品氧化镍的镍冶炼厂车间设计。 高镍镜分离后的硫化镍最早是用烧结机、多膛炉或回转窑等设备焙烧脱硫，然后用电炉或反射炉还原熔铸成的粗镍阳极。20世纪50~60年代加拿大国际镍公司和前苏联北方镍公司先后开发应用了流态化焙烧—还原熔炼工艺，制成粗镍阳极。国际镍公司还应用流态化焙烧生产一部分商品氧化镍。中国吉林镍业公司于1989年建成了流态化焙烧生产氧化镍的车间。50年代，加拿大汤普逊冶炼厂首次将硫化镍铸成阳极板送去电解，60年代，中国成都电冶厂和金川有色金属公司也采用了这一工艺。 工艺流程包括硫化镍流态化焙烧、氧化镍的还原熔炼和硫化镍反射炉熔化。 (l)硫化镍流态化焙烧。国际镍公司的流态化焙烧工艺流程如图所示。硫化镍制粒后在1100℃的温度下焙烧产出的氧化镍既可以还原熔铸成粗镍阳极板送电解精炼，也可以作为商品氧化镍出售。 硫化镍精矿)遥热盘~ t90%Ni)一二一一---一.一 硫化镍流态化焙烧生产氧化镶工艺流程示意图 (2)氧化镍的还原熔炼。通常采用炼钥用的电弧炉，以石油焦作还原剂，在1600~1700℃的温度下还原成金属镍熔体，除去杂质后铸成阳极板送电解精炼，也可以采用反射炉还原熔炼。 (3)硫化镍反射护熔化。熔化后并铸成硫化镍阳极板送电解精炼。金川有色金属公司镍冶炼厂采用了这一工艺流程。 主要设备有硫态化焙烧炉、电炉和反射炉。(l)硫态化焙烧炉。国际镍公司的流态化焙烧炉直径为3.Zm，高为10.7m，直线速度为Zm/s，床能率为24t/(耐·d)。每座焙烧炉每天可焙烧3oot硫化镍。(2)电炉。氧化镍还原用电炉通常采用炼钢用的电弧炉。有3t、st、st和lot几种规格，其功率为1500~25。。kV·A。(3)硫化镍熔化反射炉。以重油为燃料，炉床面积为20~40 mZ，床能率为3.st/(mZ·d)。 车间配置与重有色金属冶炼厂其他反射炉、电炉、流态化焙烧炉的车间配置基本相同。 技术经济指标主要技术经济指标如表。 裸阳极板和权化裸制备技术经济指标硕于