1) discontinuous muhilayers
不连续多层膜
1.
Fe-SiO_2 discontinuous muhilayers have been fabricated on glass substrates by dc facing-target magnetron sputtering and rf sputtering and subsequently annealed in situ vacuum.
通过扫描探针显微镜对样品的微结构进行了分析,发现在400℃时形成典型的不连续多层膜结构,磁性颗粒比较均匀的分散在母体当中。
2) multiplayered discontinuity
多层不连续
3) discontinuous multilayer films
非连续多层膜
1.
The GMR and magnetic property of the discontinuous multilayer films were measured with four-point probe device and Vibration Sample Magnetometer (VSM.
用射频磁控溅射及离子束改性技术制备了由接近零磁致伸缩三元合金NiFeCo和非磁性金属Ag组成的多层膜与非连续多层膜，研究了注入Co离子、退火温度和多层膜结构对NiFeCo／Ag非连续多层膜的表面形貌、巨磁电阻效应(GMR)和磁性的影响；用四探针法和振动样品磁强计分别测试了非连续多层膜的巨磁电阻效应和磁性能；用X射线衍射仪分析了非连续多层膜的相结构；用俄歇能谱仪分析了非连续多层膜的成份；用扫描电镜、原子力显微镜观测了非连续多层膜的表面形貌。
4) discontinuous magnetic metal/insulator multilayers
不连续磁性金属绝缘体多层膜
1.
A series of discontinuous magnetic metal/insulator multilayers (DMIM) of Co/SiO_(2) is fabricated using radio_frequency magnetron sputtering technique.
用射频磁控溅射方法制备了系列Co SiO_2 不连续磁性金属绝缘体多层膜 (DMIM) 。
5) discontinuous film
不连续膜
6) continuous film
连续膜层
补充资料：全氟羧酸-磺酸多层阳离子交换膜
分子式：
CAS号：
性质：又称全氟羧酸-磺酸多层阳离子交换膜，需在膜的一面形成一羧酸膜层。其制法是将全氟磺酸膜片与全氟羧酸膜片加热层压而成，或在全氟磺酸膜的一面经化学处理，使—SO3H转换成—COOH基。这种离子膜一面为—SO3H基，另一面为—COOH，用聚四氟乙烯织物增强，在氯化钠电解制碱中的电流效率为95%左右。
CAS号：
性质：又称全氟羧酸-磺酸多层阳离子交换膜，需在膜的一面形成一羧酸膜层。其制法是将全氟磺酸膜片与全氟羧酸膜片加热层压而成，或在全氟磺酸膜的一面经化学处理，使—SO3H转换成—COOH基。这种离子膜一面为—SO3H基，另一面为—COOH，用聚四氟乙烯织物增强，在氯化钠电解制碱中的电流效率为95%左右。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条