1)  ultimate bond strength
极限粘结强度
1.
The paper expounds the important significance of the bond behavior study of the corroded reinforced concrete,introduces briefly the experimental method of the bond behavior test,reviews the research results of the corrosion bond constitutive relation,the deterioration law of the ultimate bond strength after the corrosion,the bond finite element simulation after the corrosion.
阐述了锈蚀钢筋与混凝土粘结性能研究的重要意义,简要介绍了粘结性能测试的试验方法,回顾与评述了锈蚀粘结本构关系、锈蚀后极限粘结强度退化规律、锈蚀后粘结的有限元模拟等研究领域的成果。
2.
Based on the result of reinforced concrete accelerated corrosion experiment,the constitutive relation between corrosion rate and ultimate bond strength was given.
根据钢筋快速锈蚀试件的粘结破坏试验结果 ,考虑混凝土保护层厚度、混凝土强度、钢筋直径、钢筋种类和钢筋位置 5种因素对锈蚀率与粘结强度关系的影响 ,给出了钢筋锈蚀率与钢筋混凝土极限粘结强度的本构关系。
3.
The result shows that the ultimate bond strength and the slippage rise at first and then drop with the increase of the corrosion rate under the same fatigue load.
研究表明:疲劳荷载强度相同,极限粘结强度和滑移差值随着钢筋锈蚀率的增加,呈现出先升后降的趋势,即当钢筋锈蚀率小于2%时,其疲劳极限粘结强度上升;而当钢筋锈蚀率大于4%时,其疲劳极限粘结强度下降。
2)  structural limits
结构强度极限
3)  limit viscosity
极限粘度
1.
The impact of reaction conditions on the limit viscosity of PAA was studied,and fouling inhibition and anti-oxidation performances of polymers with different limit viscosities were evaluated.
研究了合成条件对聚丙烯酸(PAA)极限粘度的影响,评定了不同极限粘度聚合物的阻垢性能和耐氧化性能。
4)  bond strength
粘结强度
1.
Effect of thickness on bond strength of soft liner materials for denture;
厚度对义齿软衬材料粘结强度的影响
2.
Study of chemical etching on increasing bond strength of light-cured composite to pure titanium;
用酸蚀法提高纯钛与光固化冠桥树脂粘结强度的研究
3.
Bond strength between tooth and base bracket with two bracket base designs: An in vitro comparative study.;
两种底板托槽体外粘结强度的对比研究
5)  Adhesive strength
粘结强度
1.
The putty shows a good property of waterproofing and adhesive strength.
制备了一种新型的外墙用粉体腻子,通过在配方中添加胶粉提高了腻子的耐水性能和粘结强度;干粉腻子中的胶粉与水泥水化物形成空间立体网状结构,使得腻子成为一个致密的整体;讨论了填料对腻子性能的影响,通过加入各类助剂,有效提高了腻子的防开裂性、抗渗性、施工性等性能。
2.
The factors affecting the film adhesive strength were investigated,including hydrolysis solvents,hydrolysis time,concentration of solution,and ageing temperature.
研究了水解溶剂、水解时间、溶液浓度和固化温度对硅烷膜与基体粘结强度的影响,揭示了结合机理。
3.
The adhesive strength and thermal stability of acrlamide-acrylate copolymer un- der the conditions of high temperature were studied.
扼要介绍了丙烯酰胺—丙烯酸酯共聚树脂的溶解性能,粘结性能,以标准砂为粘结对象,研究了共聚树脂的常温粘结强度,热稳定性,高温热强度等。
6)  adhesion strength
粘结强度
1.
In order to enhance interfacial adhesion strength,RFL(resorcin-formaldehyde-latex) is used to treat the surface of PET cord.
帘子线被广泛应用于橡胶增强复合材料的骨架材料,为提高涤纶帘子线与橡胶的粘结强度,通常采用RFL(间苯二酚—甲醛—胶乳)对帘子线表面进行预处理。
2.
The effect of surface corona discharge modification of UHSPE fiber on interfacial adhesion strength of UHSPE fiber/epoxy resin was investigated.
介绍了一种新型高性能有机纤维———超高强度聚乙烯(UHSPE)纤维的性能及应用,研究了其表面经电晕放电改性对UHSPE纤维 环氧树脂界面粘结强度的影响。
3.
The stability of hydrolysis and adhesion strength of PU are not good.
聚氨酯的水解稳定性较差,粘结强度偏低。
补充资料:粘结强度


粘结强度
bonding strength

  n janjje qjangdu粘结强度(bonding strength)两种材料粘结在一起时,单位界面之间的粘结力。用耐火砖砌筑各种窑炉时,通常在砖与砖之间需用耐火泥浆粘结;某些不定形耐火材并(如投射料、喷涂料、喷补料等)在使用、施工时,要有一定的粘结能力,以使其有效地粘结于施工基体。为了考察粘结剂的性能,确定加入粘结剂的种类和数量,需要测定粘结强度. 中国测定耐火泥浆常温粘结强度的试验方法,分为抗折粘结强度(GB5o24·3)和抗剪粘结强度(GB5o24·4).抗折粘结强度试验方法的要点是用泥浆粘结成试样(图1),在抗折强度测定仪上进行抗折试验。(图2)介 图2测定抗折粘结强度方法示意图按下式计算抗折粘结强度: R=些 ZbhZ式中R为抗折粘结强度,MPa;F为试样粘结面断裂时的最大载荷,N;L为两支撑辊间的中心距,mm;b为粘结面处试样的宽度,mm;h为粘结面处试样的高度,mm。 抗剪粘结强度的试验方法,是在两块试样之间用耐火泥浆粘结(图3),干燥后进行剪切试验。 { 阵界‘ 图3测定杭剪粘结强度用试样示意图结果的计算如下: _F 万.~一;州 ~.A式中刀。为抗剪粘结强度;F为试样粘结面断裂时最大载荷;A为试样的粘结面积。 此外,在科研工作中还设计过一些其他方法,如拉伸法(图4)、剪切法(图5)。一自缪一羚 图4拉伸法测定粘结强度示意图一介结界面异 图5剪切法测定粘结强度示意图 不论采取何种方法,应选用自身强度大于被测泥浆粘结强度的试块,否则会出现试块断裂而粘结界面没有断开的现象。 (王通荣)
  