1) Polymer of polyglycolic acid and polylactic acid
聚羟乙酸/聚乳酸共聚物
2) PLGA
聚乳酸-羟基乙酸共聚物
1.
Construction of PLGA Release Microspheres with Adjustable Acidic Degradation Properties
酸性可调的聚乳酸-羟基乙酸共聚物微球的制备
2.
Objective To prepare PLGA fiber scaffolds by electrospinning process and investigate the influence of preparation parameters on the structure of the scaffolds.
目的以聚乳酸-羟基乙酸共聚物(PLGA)为材料,采用静电纺丝方法制备纤维支架,考察制备参数对纤维支架结构及纤维直径的影响规律。
3.
METHODS Injectable microspheres were prepared by double emulsion in liquid drying process,using poly(lactic-co-glycolic acid)(PLGA) as carrier.
方法采用复乳-液中干燥法,以聚乳酸-羟基乙酸共聚物(PLGA)为成球材料制备胸腺五肽微球,并采用正交设计L9(34)对处方进行优化。
3) PLGA(PLGA)
聚乳酸/羟基乙酸共聚物
4) Poly(D,L-lactic-co-glycolic acid) (PLGA)
聚乳酸羟乙酸共聚物
5) poly(lactide-co-glycolide)
聚(乳酸/羟基乙酸)共聚物
6) poly(lactic-co-glycolic acid)
乳酸-羟基乙酸共聚物
1.
Poly(lactic acid) (PLA) and poly(lactic-co-glycolic acid) (PLGA) are the most commonly used polymer carriers in the development of protein/peptide microspheres.
缓释微粒给药系统是蛋白质/多肽药物传输系统的一个重要研究方向,聚乳酸和乳酸-羟基乙酸共聚物是制备缓释微球最常用的载体材料。
2.
Objective:To prepare paclitaxel-loaded poly(lactic-co-glycolic acid)(PLGA)sus- tained release microsphere for injection.
目的:以乳酸-羟基乙酸共聚物(PLGA)为材料,制备用于肿瘤内注射的紫杉醇PLGA长效缓释微球。
补充资料：聚羟乙酸纤维
分子式：
分子量：
CAS号：
密度：1.5～1.6
熔点：224～226℃
用途：可作为手术缝线使用，在伤口恢复的7～11天内，强度不下降，60天后就能分解被体内吸收，无需再拔除丝线。
制备或来源：由聚羟基乙酸纺制而成。
备注：纤维线密度3.3～11分特，强度4.4～8.8厘米/分特，伸长率15～35%。纤维在碱性介质中不稳定，容易水解。
分子量：
CAS号：
密度：1.5～1.6
熔点：224～226℃
用途：可作为手术缝线使用，在伤口恢复的7～11天内，强度不下降，60天后就能分解被体内吸收，无需再拔除丝线。
制备或来源：由聚羟基乙酸纺制而成。
备注：纤维线密度3.3～11分特，强度4.4～8.8厘米/分特，伸长率15～35%。纤维在碱性介质中不稳定，容易水解。