1) corrosion in molten carbonate
熔融碳酸盐腐蚀
2) Molten carbonate
熔融碳酸盐
1.
Study on kW-scale molten carbonate fuel cell stacks;
千瓦级熔融碳酸盐燃料电池组
2.
It is shown that the anodic reaction in molten carbonates is the oxidation of metals and CO 2- 3, and the cathodic reaction is the reduction of O 2- 2 formed by the reaction of CO 2- 3 with the dissolved oxygen.
在熔融碳酸盐中,阳极极化是金属与CO2-3的氧化、阴极极化则是O2-与CO2-3的还原。
3.
A little NiO dissolved in molten carbonate will cause the shortage of fuel cell, which is one of the key technical problems before molten carbonate fuel cells come into market.
NiO在碳酸盐中的微量溶解,会造成电池内部的短路,是熔融碳酸盐燃料电池实用化须要解决的关键问题。
4) molten salt corrosion
熔盐腐蚀
1.
The high temperature molten salt corrosion behaviours of SiC ceramics is summarized systematically, including chemistry of molten salt, corrosion kinetics and change of material properties in course of corrosion.
系统总结了碳化硅陶瓷的高温熔盐腐蚀行为 ,包括熔盐的化学性、腐蚀动力学、材料在腐蚀过程中的性能变化 ,并提出了今后提高碳化硅陶瓷耐熔盐腐蚀的研究方
5) molten carbonate process
熔融碳酸盐法(能)
补充资料:熔融碳酸盐燃料电池
分子式:
CAS号:
性质:以熔融碱金属碳酸盐的混合物组成低共熔体系作电解质,以氧化镍为正极、镍为负极的一种燃料电池。燃料用氢和一氧化碳,氧化剂为空气(氧,含一定量的反应产物二氧化碳)。放电时的电化学反应:正极:1/2O2+CO2+2e—=CO32-负极:CO+H2O=CO2+H2H2+CO32--2e—=H2O+CO2电池反应:O2+CO+H2=H2O+CO2工作温度约为650℃。以150mA/cm2电流密度放电时,工作电压可达0.75V。不使用贵金属催化剂,可间接使用天然气或煤作燃料,通过在电池外或直接在电池内重整生成水煤气供使用,污染较少。其成套燃料电池系统(包括维持温度及利用余热的热交换系统)的能量转化效率可达60%~65%。美国、日本等国已安装成100kW级模型电站试运行。
CAS号:
性质:以熔融碱金属碳酸盐的混合物组成低共熔体系作电解质,以氧化镍为正极、镍为负极的一种燃料电池。燃料用氢和一氧化碳,氧化剂为空气(氧,含一定量的反应产物二氧化碳)。放电时的电化学反应:正极:1/2O2+CO2+2e—=CO32-负极:CO+H2O=CO2+H2H2+CO32--2e—=H2O+CO2电池反应:O2+CO+H2=H2O+CO2工作温度约为650℃。以150mA/cm2电流密度放电时,工作电压可达0.75V。不使用贵金属催化剂,可间接使用天然气或煤作燃料,通过在电池外或直接在电池内重整生成水煤气供使用,污染较少。其成套燃料电池系统(包括维持温度及利用余热的热交换系统)的能量转化效率可达60%~65%。美国、日本等国已安装成100kW级模型电站试运行。