4) longitudinal crack
纵裂
1.
Analysis and Improved Process Practice on Surface Longitudinal Crack of Concasting Slab of Steel 09CuPTiRE;
09CuPTiRE钢连铸板坯表面纵裂分析和改进工艺实践
2.
The source of longitudinal crack in surface of thin slab;
连铸薄板坯表面纵裂纹的产生根源
3.
Analysis on Surface Longitudinal Crack of Concasting Slab of Heat Resistant Stainless Steel 310S and Process Improvement
310S耐热不锈钢连铸板坯表面纵裂分析和工艺改进
5) longitudinal cracking
纵裂
1.
Causes of longitudinal cracking of medium carbon SS400 thin slab casting and its countermeasures;
薄板坯连铸中碳钢SS400纵裂原因分析及控制措施
2.
The factors causing longitudinal cracking in continuously cast steel slabs have been investigated by analysis of the data of CC process.
根据宝钢连铸大生产实绩 ,调查了影响板坯纵裂的因素 ,分析了连铸板坯发生纵裂的原因 ,通过采取一定的措施 ,使连铸坯纵裂指数有一定的改善。
3.
In this paper,the factor causing longitudinal cracking have been investigated by analysis of the data of Slab Continuous Caster in Qian an Iron&Steel Co.
本文根据迁钢公司板坯铸机生产中碳高锰钢的生产实践调查影响纵裂的因素,分析了纵裂发生的原因,通过采取一定的措施,使得中碳高锰钢的纵裂得到了控制。
6) longitudinal crack
纵裂纹
1.
Cause analysis and control measures of longitudinal cracks on the surface of continuous casting slabs;
连铸板坯表面纵裂纹原因分析及控制措施
2.
Controll the longitudinal crack of thin slab;
薄板坯连铸纵裂纹的控制
3.
The pattern of the longitudinal cracks on surface of continuous casting slab was summarized.
综述了连铸板坯表面纵裂纹的形貌,分析了纵裂的形成机理及影响纵裂的各种因素,为采取措施减轻和避免这种质量缺陷提供依据。