1) erichsen test
杯突成形性
1.
Increasing roughness of steel sheet surface is suitable for erichsen test of the laminated steel sheet.
用聚氨酯或酚醛树脂氯丁橡胶作夹层 的层压减振复合钢板具有良好的杯突成形性；提高钢板表面粗糙度，有利于改善复合钢板的 杯突成形性。
2) cup depth
杯突
3) Cupping test value
杯突值
4) cupping tester
杯突机
5) cupping value
杯突值
1.
The result indicates that the cupping value is increasing with increase of thickness,the cupping value is decreasing with increase of blank holding force.
在GBS-60型半自动数显杯突机上对不同批次、不同厚度的1100铝箔材进行了检验,找出了影响杯突值准确性的主要因素——试样厚度、压边力与冲杯速度。
2.
The cupping value of lubricated aluminum alloy sheet is studied by BCS-30D general sheet metal test machine.
在BCS-30D通用板材成形性试验机上,对铝合金薄板的杯突值进行了不同润滑条件的试验研究。
6) Erichsen tester
杯突试验
1.
and compared with those parameters of 6010 aluminum alloy; By using machine performance parameters of 6061 aluminum alloy ,finite element software eta/DYNAFORM of Sheet Forming made the numerical simulation of Erichsen tester process of 6061 aluminum alloy sheet,and the result of numerical simulation compared with actual Erichsen tester.
利用电子万能试验机、扫描电镜等手段,对6061铝合金板材的拉伸性能进行了研究,并与6010铝合金的各项力学性能参数进行了比较；利用拉伸试验所测的力学性能参数,用板料成形有限元分析软件 --Dynaform 对6061铝合金的杯突过程进行仿真,并与真实的杯突试验进行了比较,分析了6061铝合金薄板的冲压成形性能。
参考词条
补充资料：杯突试验仪
分子式：
CAS号：
性质：又称顶杯或压陷试验仪。杯突试验仪是由试板夹紧器和可上下移动的冲头和固定的冲模三部分组成(见图)试验时，将涂有待试涂膜的样板(钢板)涂膜朝下、背面朝上，夹紧固定在冲模中心，然后使冲头恒速推向涂漆试板的背面，将样板顶入冲模内，形成杯突状变形，然后观察正面漆膜是否开裂或从钢板上剥落。漆膜破坏时冲头压入的最小深度，即为测得的杯突指数[也称艾利克逊数(Erichsen)]以mm表示。杯突试验与耐冲击强度所表现的性能不同。这是对底材伸长情况下，对涂膜的强度、弹性和附着力的综合考察。杯突试验对卷材工业，制罐工业等所用的卷钢涂料，罐头涂料是不可缺少的项目。
CAS号：
性质：又称顶杯或压陷试验仪。杯突试验仪是由试板夹紧器和可上下移动的冲头和固定的冲模三部分组成(见图)试验时，将涂有待试涂膜的样板(钢板)涂膜朝下、背面朝上，夹紧固定在冲模中心，然后使冲头恒速推向涂漆试板的背面，将样板顶入冲模内，形成杯突状变形，然后观察正面漆膜是否开裂或从钢板上剥落。漆膜破坏时冲头压入的最小深度，即为测得的杯突指数[也称艾利克逊数(Erichsen)]以mm表示。杯突试验与耐冲击强度所表现的性能不同。这是对底材伸长情况下，对涂膜的强度、弹性和附着力的综合考察。杯突试验对卷材工业，制罐工业等所用的卷钢涂料，罐头涂料是不可缺少的项目。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。