1) Rehydration
[英][,ri:hai'dreiʃən] [美][,rihaɪ'dreʃən]
再水化
1.
According to the rehydration characteristics of dehydrated phases,a kind of new cementious material system can be prepared with gypsum and fly ash.
根据水泥水化产物脱水相具有再水化能力的特点,结合粉煤灰、磷石膏等矿物材料的化学反应特性,组成一个新的胶凝材料体系。
2.
Ther-mogravimetric–differential scanning calorimeter (TG–DSC), X-ray diffraction, infrared and 29Si nuclear magnetic resonance were used to investigate the structural characteristics, rehydration ability and rehydrating products structure of dehydrated phases prepared at 400, 650 ℃ and 900 ℃.
将水泥石在不同温度进行低温煅烧,得到不同的脱水相物质,通过热重–差示扫描热分析、X射线衍射、红外光谱及29Si核磁共振等对水泥石在400,650℃及900℃的脱水相结构特征及其再水化性能、再水化产物的结构特征进行研究。
2) reconstitution solution
再水化液
1.
Effect of reconstitution solutions on the recovery of lyophilized red blood cells;
再水化液因素对冰冻干燥保存后红细胞回收率的影响
3) rehydration degree
再水化程度
1.
The samples with different content of dehydrated phase of hydrated cement paste were prepared to study the influence of heat treatment on their rehydration abilities which were evaluated with the water requirements for normal consistency,the initial setting time,rehydration degree and compressive strength.
试验表明:在一定温度下,随着脱水相含量的增大,脱水水泥石粉的标准稠度用水量显著增大,初凝时间逐渐缩短,再水化程度发展加快,抗压强度逐渐减小,即热处理后旧水泥石中脱水相的含量影响其再水化性能。
2.
5) subjected to high temperatures were evaluated by the water requirements of standard consistency,the setting times,the compressive strength,rehydration degree and mineral analysis by XRD.
结果表明:随着处理温度的提高,旧水泥浆的标准稠度需水量显著增大,初、终时间逐渐缩短,抗压强度呈上升趋势,在800℃左右达到最大值;热处理后旧水泥浆的再水化程度发展很快,1 d水化程度达到60%,28d水化程度接近90%。
4) Oral Rehydration Salts
再水化溶液
5) repulping(acidulation) and water washing
再浆(酸化)水洗
6) regasification in steam
水蒸气再气化
补充资料：1,2-二氨基环己四乙酸-水化物
CAS: 125572-95-4
分子式: C14H22N2O8.H2O
分子质量: 364.35
熔点: 210℃
中文名称: 1,2-二氨基环己四乙酸-水化物
英文名称: trans-1,2-diaminocyclohexane-n,n,n',n'-tetraacetic acid monohydrate
分子式: C14H22N2O8.H2O
分子质量: 364.35
熔点: 210℃
中文名称: 1,2-二氨基环己四乙酸-水化物
英文名称: trans-1,2-diaminocyclohexane-n,n,n',n'-tetraacetic acid monohydrate
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条