1) calcium metaphosphate whisker
偏磷酸钙晶须
1.
In order to increase the strength and load capability of poly L-lactide(PLLA) for fracture innerfixation,the composite materials of PLLA and β-calcium metaphosphate whisker(CMPw) with the aspect ratio of 30～50 prepared by crystallizing in the glass were obtained.
为了提高骨折内固定材料聚乳酸的力学强度及承载能力,通过玻璃结晶化方法制备得到长径比为30~50的偏磷酸钙晶须(CMPw),将CMPw与左旋聚乳酸(PLLA)复合,制得抗压强度为80MPa,抗弯强度为40MPa,断裂强度达到170MPa的复合材料。
2) calcium sulfate whiskers
硫酸钙晶须
1.
Effect of calcine on crystal structure and stability of calcium sulfate whiskers;
煅烧对硫酸钙晶须结构及稳定性的影响
2.
Study on the surface properties and hydration meehanism of calcium sulfate whiskers;
硫酸钙晶须表面性质及水化机理研究
3.
Gypsum can processing into α semi hydrated gypsum,ultrafine gypsum powder and calcium sulfate whiskers etc.
石膏可深加工成α－半水石膏、石膏超细粉及硫酸钙晶须等。
3) CaCO3 whisker
碳酸钙晶须
1.
In this paper,the change of filled paper property is studied with aragonite CaCO3 whisker.
文章采用自制文石型碳酸钙晶须替代传统方解石型碳酸钙,研究其填充纸张性能的变化,结果表明:同样条件下,文石型碳酸钙晶须较传统方解石型碳酸钙填料有更高的留着率,更小的纸张强度降低率。
4) Calcium sulphate whisker
硫酸钙晶须
1.
Calcium sulphate whisker is a new nonmetal material prepared from gypsum.
硫酸钙晶须是由生石膏制备而成的新型非金属材料。
2.
The expansive prospect of preparing calcium sulphate whisker from marine gypsum is also pointed out in the article.
介绍了盐石膏的理化性质,综述了我国海盐工业废渣盐石膏在水泥、石膏建材等建筑领域以及对盐石膏的深加工等方面的综合利用研究现状,并指出利用盐石膏制备硫酸钙晶须具有广阔的发展前景。
3.
Properties of potassium titanate whiskers and calcium sulphate whiskers modified epoxy resin were investigated.
应用硅烷及钛酸酯等偶联剂对钛酸钾晶须及硫酸钙晶须进行表面处理 ,考察晶须对环氧树脂力学性能、工艺性等的影响。
5) calcium carbonate whiskers
碳酸钙晶须
1.
Hydrothermal synthesis of calcium carbonate whiskers by using waste phosphogypsum as raw materials;
以废弃磷石膏为原料水热合成碳酸钙晶须的研究
2.
The effects of potassium titanate whiskers and calcium carbonate whiskers and needle-like wollastonite on the tribological properties of braking friction material were studied.
研究了分别填充钛酸钾晶须、碳酸钙晶须、针状硅灰石对刹车片摩擦磨损性能的影响。
3.
Calcium carbonate whiskers are characteristic of low cost, high whiteness and big package, and they are widely used for improving the mechanic performance of polymer composite.
碳酸钙晶须具有成本低、白度高、填充量大的特点，因而大量地用于改善聚合物复合材料的力学性能。
6) calcium sulfate whisker
硫酸钙晶须
1.
Study on the key technology in preparation of calcium sulfate whisker;
硫酸钙晶须制备过程中的关键技术研究
2.
Study on the preparation and morphology of calcium sulfate whisker by hydrothermal synthesis method;
水热法制备硫酸钙晶须及其结晶形态的研究
3.
Study on the treatment of emulsified-oil containing wastewaterwith calcium sulfate whisker;
硫酸钙晶须去除废水中乳化油的研究
补充资料：偏磷酸钙
分子式：Ca(PO3)2
CAS号：
性质：密度2.82g/cm3。熔点970～980℃。有玻璃状和结晶状两种。玻璃状者纯品为无色透明的聚合体[Ca(PO3)2]n。在空气中有微吸湿性。在水中能极缓慢溶解和水解，但当有酸或水蒸气存在时，能迅速分解成磷酸二氢钙。工业品呈浅绿色，总磷64%～67%P2O5，枸溶性磷62%～66%P2O5是一种高浓度枸溶性磷肥。结晶状者呈白色，不溶于水，也难溶于柠檬酸溶液中，不能用作肥料，其他用途也未发现。由磷在空气中燃烧成五氧化二磷，再与磷矿粉在高温和水蒸气存在下而制得。可作基肥施用。对豆科、牧草、谷物、小麦的增产效果与等磷量的过磷酸钙相当或稍高一些。偏磷酸钙还可用于生产六偏磷酸钠的添加原料。