1) Valvoplasty
瓣膜成形
1.
In vitro Study of Laser Cardiac Valvoplasty and Endothelialization of Valve;
激光心脏瓣膜成形及内皮细胞种植的实验研究
2) valvuloplasty
[英]['vælvjələ,plæsti:] [美]['vælvjələ,plæsti]
瓣膜成形
1.
Clinical study of valvuloplasty on valve disease Cardiac Surgery department, second affiliated hospital of zhengzhou university;
心脏瓣膜成形术的临床研究——附700例临床研究报告
4) Valvoplasty
瓣膜成形术
1.
Objective:To introduce the surgical techniques and outcome of the valvoplasty for the organic tricuspid disease utilizing autogeneous pericardium.
目的:介绍应用自体心包行器质性三尖瓣病变瓣膜成形术的方法和疗效。
5) Valve annuloplasty
瓣膜成形术
1.
Methods During operations,23 cases of cardiac defect were repaired with unidirectional valved patch and intered catheters in order to inject prostaglandin E1(PGE1) into pulmonary artery,and monitor pulmonary artery pressure(PAP) after operation,and cases with mitral incompetence(MI) were treated with mitral valve annuloplasty.
结论单向活瓣补片修补缺损、肺动脉内置管泵入PGE1能明显降低PAP,改善血气指标,增加围手术期安全性,同期行必要的瓣膜成形术有利于降低PAP,心脏间隔缺损并重度PH应严格把握手术适应证。
6) balloon valvuloplasty
球囊瓣膜成形术
1.
Application of Transesophageal Echocardiography in the Percutareous Transvenous Balloon Valvuloplasty;
经食管超声心动图在球囊瓣膜成形术中的应用
补充资料：主要射出成形材料成形时应注意事项
■主要射出成形材料成形时应注意事项
品 名 注 意 事 项
PVC
聚氯乙烯
1. 产品种类范围非常广（硬质、软质、聚合物等），成型条件各有不同，从熔融至分
解之温度范围很小，尤须注意加热温度。
2. 附着水分少，但成型周期尽可能减少（50℃~60℃热风干燥）。
3. 成型机方面，与材料直接接触的部位须电镀或采用不锈钢以防热分解所产生的盐酸
侵蚀。射出压力2100kg/cm2程度。
4. 所有塑料当中必须是细心注意温度调节。
5. 浇口附近易产生流纹，故射出操作后，柱塞不要后退使浇口充分固化后再瞬间退后为宜。
6. 加热之初温不宜高，特别注意熔融情形。第二级加热温度较高，且尽可能使成形周
期缩短，比较安全。
PA
聚醯胺树脂
1. 成型温度比其它材料高，故采用油加热的成形机较适当。
2. 吸湿性大，必须充分干燥。水分对成型品的品质影响甚大（80℃热风干燥约5~6小时）。
3. 须退火以消除内部歪斜。
PP
聚丙烯
1. 同PE，但成形温度必须较高。熔融温度170℃，超过190℃则流动性大增，则毛边增加，
易产生接缝及凹入情形。
PC
聚碳酸脂
1. 吸湿性比尼龙小，但若有些微之水分存在则成型品产生其它色泽或气泡，故必须密封
干燥同时成形时也须预备干燥（120℃之温度4小时）。
2. 加热温度超过320℃时则产生热分解，成品变色，故特别注意温度调节，又成型时的温度调节也非常重要，须特别注意其最低温度、最低时间。
3. 须退火以消除内部歪斜（130℃~135℃，1小时程度为准）。