1) heat-dispersion suspension complex method
悬浮液热分散复合法
1.
A series of macroporous calcium polyphosphate/chitosan(CPP/CS) composite rod and microporous CPP/CS composite particle were synthesized with CPP and CS using two technologies by a heat-dispersion suspension complex method.
采用自行设计的悬浮液热分散复合法,用硬脂酸(Sad)作为致孔剂,通过复合-沉析-浸溶-漂洗-干燥的工艺制备大孔聚磷酸钙/壳聚糖(CPP/CS)复合材料棒材。
2.
A series of porous CS/CPP composites were synthesized with CS(chitosan),CPP(calcium polyphosphate)and Sad(stearic acid)was used as the inducing porous substance by heat-dispersion suspension complex method.
采用自行设计的悬浮液热分散复合法,通过复合-沉析-浸溶-漂洗-干燥的工艺过程,用硬脂酸(Sad)作为致孔剂,合成出了不同配比的用于骨修复的多孔壳聚糖(CS)/聚磷酸钙(CPP)复合组织工程材料。
2) highly dispersed suspension
高分散悬浮液
3) Suspension-emulsion combined polymerization
悬浮-乳液复合聚合
4) hybrid dispersions
复合分散液
1.
Water-borne polyurethane-epoxy-acrylate(WPUEA) hybrid dispersions was prepared using toluene diisocyanate(TDI-80),polyether polyol(N220),epoxy resin(E20) and methyl methacrylate(MMA) as main raw materials.
以甲苯二异氰酸酯(TDI-80)、聚醚二元醇(N220)、环氧树脂(E20)和甲基丙烯酸甲酯(MMA)等为原料,通过原位聚合,制备了水性聚氨酯-环氧树脂-丙烯酸(WPUEA)复合分散液。
5) buoyant hydrothermal plume
悬浮热液柱
6) suspension dispersive agent
悬浮分散剂
1.
Synthesis and characterization ofinorganic suspension dispersive agent——active phosphate calcium;
无机悬浮分散剂——活性磷酸钙的研制与表征
补充资料：导电填料分散复合法
分子式：
CAS号：
性质：是制备复合型高分子材料的主要方法之一。其核心是采用各种混合方法使导电填料在绝缘性基体-高分子材料中均匀分布，构成以基体高分子材料为连续相，导电填料为分散相的复合导电材料。其导电机理有人认为是填充材料在基体中构成网状的连续导电通路，也有人认为是在导电微粒之间距离足够小时构成所谓导电“隧道”，其证据为在电子显微镜下绝大多数导电微粒并未接触，形成网络。这种方法的主要优点在于操作简便，可以采用多种常见的、价格低廉的材料，并能满足不同使用要求。是目前使用最为广泛的复合制备方法。
CAS号：
性质：是制备复合型高分子材料的主要方法之一。其核心是采用各种混合方法使导电填料在绝缘性基体-高分子材料中均匀分布，构成以基体高分子材料为连续相，导电填料为分散相的复合导电材料。其导电机理有人认为是填充材料在基体中构成网状的连续导电通路，也有人认为是在导电微粒之间距离足够小时构成所谓导电“隧道”，其证据为在电子显微镜下绝大多数导电微粒并未接触，形成网络。这种方法的主要优点在于操作简便，可以采用多种常见的、价格低廉的材料，并能满足不同使用要求。是目前使用最为广泛的复合制备方法。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条