1) Celloidin section
火棉胶切片
2) Thin section of collodion
火棉胶薄层切片
3) collodion microtomy
火棉胶切片技术
1.
Methods: The serial sheet frontal sections of the superior orbital fissure region were obtained by collodion microtomy in 5 a- dult cadaver heads and were observed.
方法：采用火棉胶切片技术对5例(10侧)成人眶上裂区标本进行连续薄层冠状断层解剖学观察。
2.
Methods (1)We observed the serial sheet sections of the optic apex region obtained using collodion microtomy in 4 adult cadaver heads; (2)High resolution CT scanning and three dimensional images of the optic apex region were observed and measured in 10 adult volunteers; (3)High resolution magnetic resonance images of the optic apex region were obse.
方法 ①采用火棉胶切片技术对4例(8侧)成人眶尖区标本进行连续薄层断层解剖学观察；②使用高分辨力CT及三维重建技术观测10例(20侧)志愿者眶尖区；③观测5例(10侧)志愿者眶尖区高分辨力MRI断层扫描图像；④对30例(60侧)成人干颅骨标本和15例(30侧)成人湿性头颅标本的眶尖区结构进行显微解剖；⑤在手术显微镜和内窥镜下对3例成人头颅湿性标本模拟眶内经颅入路。
4) collodion film
火棉胶软片
5) wet collodion process
火棉胶湿版<片>法
6) collodion
[英][kə'ləudiən] [美][kə'lodɪən]
火棉胶，胶棉
补充资料：火棉胶
硝酸纤维素实际上是纤维素的硝酸酯，它是以精制短棉绒为原料，用硝酸、硫酸的混合酸进行酯化，使纤维素中的-OH基酯化成－ONO2的产物。根据纤维素中3个-OH基酯化程度的不同，就可得到不同含氮量的CN，随着酯化程度增大，台氮量升高，三硝酸纤维素的理论含氮量为14．14％。不同含氮量的硝酸纤维素有着不同的溶解度和用途。塑料用的含氮量为10．5-12．3％，胶粘剂和涂料用的为11．5％-12．2％，火药用的为11．8％-13．5％。硝酸纤维素的聚合度n＝100-3500，分子量为16200-875000。
CN为白色或微黄色絮绒状固体，无臭、易燃 、易爆，相对密度1.58-1.65，熔点160-170 ℃，闪点12．78℃，自燃温度170℃，折射率1．51。不溶于水，易溶于酮、酯、醇、醚类溶剂，硝酸纤维素对碱很敏感，容易发生皂化而脱硝。长期在光和热作用下能分解并降低含氮量。
硝酸纤维素主要用于配制溶剂型胶桔剂，粘接赛璐珞塑料制品和火药。配制火棉胶。
由于硝化纤维素性质很不稳定，易燃易爆，当温度超过40 ℃时能加速分解而发生自燃。含水25％时较安全，因此在贮运时加入30％左右的乙醇或水为湿润剂，以增加稳定性。使用前应将硝酸纤维素的水烘干，要特别注意安全、最好使用水烘箱，如果用电烘箱温控一定要可取，烘箱门不得关死，防止爆炸。中间观察时人不得面对烘箱开门，以防发生意外。
贮存于阴凉、通风的专用库房内，温度不超过30℃，远离火种和热源。
CN为白色或微黄色絮绒状固体，无臭、易燃 、易爆，相对密度1.58-1.65，熔点160-170 ℃，闪点12．78℃，自燃温度170℃，折射率1．51。不溶于水，易溶于酮、酯、醇、醚类溶剂，硝酸纤维素对碱很敏感，容易发生皂化而脱硝。长期在光和热作用下能分解并降低含氮量。
硝酸纤维素主要用于配制溶剂型胶桔剂，粘接赛璐珞塑料制品和火药。配制火棉胶。
由于硝化纤维素性质很不稳定，易燃易爆，当温度超过40 ℃时能加速分解而发生自燃。含水25％时较安全，因此在贮运时加入30％左右的乙醇或水为湿润剂，以增加稳定性。使用前应将硝酸纤维素的水烘干，要特别注意安全、最好使用水烘箱，如果用电烘箱温控一定要可取，烘箱门不得关死，防止爆炸。中间观察时人不得面对烘箱开门，以防发生意外。
贮存于阴凉、通风的专用库房内，温度不超过30℃，远离火种和热源。