1) near β titanium alloy
近β钛合金
1.
Objective:This study was intended to modify the surface of a novel near β titanium alloy Ti-5Zr-3Sn-5Mo-15Nb (TLM) by micro-arc oxidation(MAO),and evaluate the influence of MAO process on the morphology and integrin β1(Itgβ1) expression of osteoblasts cultured on TLM.
目的:采用微弧氧化(MAO)方法对近β钛合金Ti-5Zr-3Sn-5Mo-15Nb(TLM)进行表面处理,观察其对成骨细胞在其表面粘附形态及整合素表达水平的影响。
2.
The objective of this study was to modify the surface of a novel near β titanium alloy Ti-5Zr-3Sn-5Mo-15Nb (TLM) by micro-arc oxidation (MAO).
采用微弧氧化(MAO)方法对近β钛合金Ti-5Zr-3Sn-5Mo-15Nb(TLM)表面进行处理,分析其表面特性变化,并观察成骨细胞在其表面的早期粘附。
2) near β type titanium alloys
近β型钛合金
3) near-β TB10 titanium alloy
近β型TB10钛合金
4) β titanium alloy
β钛合金
1.
The sorts,development history,application range,application prospect and development direction of β titanium alloys in biomedicine and aerospace fields were introduced in this paper.
本文介绍了β钛合金的分类、在生物医学和航空航天领域的发展历史、应用范围,以及其应用前景和发展方向。
2.
The β titanium alloys developed at home and abroad are summarized and classified with Mo equivalent as standard.
本文以钼当量为标准对国内外研制的β钛合金进行了汇总和归类。
5) β-titanium alloys
β-钛合金
1.
The design and progress of the study on new β-titanium alloys as biomedical materials was introduced.
主要介绍了新型生物医用β-钛合金的设计思路及研究进展。
6) β titanium alloys
β钛合金
1.
R & D status for two kinds of high strength β titanium alloys used for springs,Timetal LCB and Ti-B20,is reviewed.
β钛合金因综合性能优异(良好的冷热成形性、时效强化效应明显、耐蚀等)成为高强钛弹簧的理想选择。
补充资料：近β钛合金
分子式：
CAS号：
性质： β稳定元素略高于临界浓度的钛合金。成分中主要含有β稳定元素钒、钼、铁、铬等。具有最高的强化效应、最高的强度(1200MPa)、较深的淬透截面(60～150mm)、良好的拉伸塑性和断裂韧性。主要有β-Ⅲ、BT22等牌号。采用真空自耗电弧炉熔炼制取。适于制造紧固件和较大截面的模锻件。
CAS号：
性质： β稳定元素略高于临界浓度的钛合金。成分中主要含有β稳定元素钒、钼、铁、铬等。具有最高的强化效应、最高的强度(1200MPa)、较深的淬透截面(60～150mm)、良好的拉伸塑性和断裂韧性。主要有β-Ⅲ、BT22等牌号。采用真空自耗电弧炉熔炼制取。适于制造紧固件和较大截面的模锻件。