1) CdTe nano-particles
CdTe纳米粒子
1.
The average size of CdTe nano-particles estimated from TEM graph was ca.
以巯基乙酸为稳定剂和表面修饰剂,在有机相中合成了平均粒径为3nm左右的CdTe纳米粒子,用胃蛋白酶改变纳米粒子的表面修饰状态并研究其系列特性。
2) Nanosized CdTe particles
纳米CdTe微粒
3) CdTe nanoparticles
CdTe纳米颗粒
4) CdTe nanocrystals
CdTe纳米晶
1.
Studies on interaction between CdTe nanocrystals and phenylalanine;
CdTe纳米晶与苯丙氨酸相互作用的研究
2.
The Study on the Mechanism of the Interaction between CdTe Nanocrystals and Phenylalanine;
CdTe纳米晶与苯丙氨酸作用机理的研究
3.
CdTe nanocrystals(NCs) were synthesized and modified by using 3-mercaptopropionic acid(MPA) in aqueous solution.
制备了水溶性的CdTe纳米晶。
5) CdTe nanocrystal
CdTe纳米晶
1.
Preparation and Optical Properties of Functional ized CdTe Nanocrystals and Self-Assembled Films
功能性CdTe纳米晶的合成及自组装膜的发光性质
2.
The CdTe nanocrystals were synthesized in aqueous solution by using thioglycolic acid as the stabilizing agent.
以巯基乙酸为配体,在水相中合成了CdTe纳米晶。
3.
Ultraviolet-vusubke soectrisciot(UV-vis),Fourier transform infrared spectrametry(FT-IR),X-ray diffraction(XRD) and photoluminescence(PL) measurements were used to investigate the as-prepared CdTe nanocrystals along with the PL properties of CdTe/PVP samples.
以巯基水相法将硫基乙酸(TGA)合成一系列不同粒径的Q态CdTe纳米晶,再与聚乙烯吡咯烷(PVP)杂化制备出具有红、黄、绿3种颜色的CdTe/PVP纳米杂化材料。
补充资料：cadmium telluride CdTe
分子式：
CAS号：
性质：周期表第II，VI族元素化合物半导体。强离子性的共价键结合。立方晶系闪锌矿型结构，晶格常数0.6477nm，为复式晶格。密度5.86g/cm3。熔点1098℃。室温禁带宽度1.50eV。电子和空穴迁移率分别为6×10-2和6.5×10-3/(V·s)。采用区域熔炼法、高压熔融法制备单晶。用于制作近红外光探测器、γ和X射线谱仪、电光调制器等。
CAS号：
性质：周期表第II，VI族元素化合物半导体。强离子性的共价键结合。立方晶系闪锌矿型结构，晶格常数0.6477nm，为复式晶格。密度5.86g/cm3。熔点1098℃。室温禁带宽度1.50eV。电子和空穴迁移率分别为6×10-2和6.5×10-3/(V·s)。采用区域熔炼法、高压熔融法制备单晶。用于制作近红外光探测器、γ和X射线谱仪、电光调制器等。